Starex PT-0180 H
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nlGMLz_StarexPT0180H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starex PT-0180 H is an acrylonitrile butadiene styrene (ABS) product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: automotive industry. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.04 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 2.3 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 104 | ASTM D785 | |
| R scale | 105 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2000 | MPa | ASTM D638 |
| -- | 2000 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 37.0 | MPa | ASTM D638 |
| Yield | 42.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 32.0 | MPa | ASTM D638 |
| Fracture | 34.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Fracture 4 | 26 | % | ASTM D638 |
| Fracture | 20 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2000 | MPa | ASTM D790 |
| -- 6 | 2100 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 59.0 | MPa | ASTM D790 |
| -- 8 | 66.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 22 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 450 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 320 | J/m | ASTM D256 |
| 23°C 10 | 36 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 6.40mm | 96.0 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 4.00mm | 92.0 | °C | ISO 75-2/B |
| 0.45 MPa, annealing, 4.00mm | 98.0 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 86.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 79.0 | °C | ISO 75-2/A |
| 1.8 MPa, annealing, 4.00mm | 92.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 97.0 | °C | ISO 306/B50 |
| -- | 102 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.5 mm | HB | UL 94 | |
| 3.0 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 85 - 95 | °C | |
| Hot air dryer | 85 - 95 | °C | |
| Drying Time | |||
| -- | 3.0 - 4.0 | hr | |
| Hot air dryer | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 180 - 200 | °C | |
| Middle Temperature | 200 - 210 | °C | |
| Front Temperature | 210 - 230 | °C | |
| Nozzle Temperature | 220 - 240 | °C | |
| Mold Temperature | 40 - 80 | °C | |
| Injection Pressure | 49.0 - 147 | MPa | |
| Back Pressure | 0.490 - 1.96 | MPa | |
| Screw Speed | 50 - 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4mm |
| 10 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPV 3440N | Teknor Apex Company | TPV | Sarlink® TPV |
| VESTOLIT® E 6507 | VESTOLIT GmbH & Co. KG | PVC, Unspecified | VESTOLIT® |
| Axiall PVC 5006 Natural | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Hylon® N1033HLUV2 | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| INEOS PP H20E-00 | INEOS Olefins & Polymers USA | PP Homopolymer | INEOS PP |