Cellidor B 501-10
| Category: | CAB , Cellulose Acetate Butyrate |
| Manufacturer: | ALBIS PLASTIC GmbH |
| Trademark: | Cellidor |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nksaYY_Cellidor-B-501-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Cellidor B 501-10 is a Cellulose Acetate Butyrate (CAB) product. It can be processed by injection molding and is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (210°C/2.16 kg) | 9.00 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 132/30) | 65.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1600 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 38.0 | MPa | |
| -- | 37.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 4.0 | % | |
| Break | 13 | % | |
| Flexural Modulus | 1650 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| -- | 46.0 | MPa | |
| 3.5% Strain | 42.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -- | 24 | kJ/m² | |
| -40°C | 4.0 | kJ/m² | |
| -20°C | 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -- | No Break | ||
| -40°C | No Break | ||
| -20°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 85.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 85.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| Circulation Dryer | 50.0 to 70.0 | °C | |
| Desiccant Dryer | 50.0 to 70.0 | °C | |
| Drying Time | |||
| Circulation Dryer | 2.0 to 4.0 | hr | |
| Desiccant Dryer | 1.0 to 2.0 | hr | |
| Processing (Melt) Temp | 190 to 235 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPE EE-1290N NAT | Teknor Apex Company | TPE | Sarlink® TPE |
| AIE PA66 60G6F | Asia International Enterprise (Hong Kong) Limited | Nylon 66 | AIE PA66 |
| ALCUDIA® LDPE CA-2130A | REPSOL | LDPE | ALCUDIA® LDPE |
| Di-Pak™ R-4243 | Hapco Inc. | TP, Unspecified | Di-Pak™ |
| Lupol® MC4352 | LG Chem Ltd. | TPO | Lupol® |