Order Products : sales@su-jiao.com
Amodel® AE-1133
| Category: | PPA , Polyphthalamide |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Amodel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nkDn72_Amodel-AE-1133.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
AMODEL A- 1133 HS is a 33% glass fiber reinforced thermally stable polyphthalamide (PPA) with high thermal deformation temperature, high bending modulus and high tensile strength. Excellent creep resistance and low moisture absorption are also characteristics of the resin. -Black: A- 1133 HS BK 324
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.48 | g/cm³ | ISO 1183/A |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.40 | % | ASTM D955 |
| Transverse flow | 0.80 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.21 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 125 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- | 13100 | MPa | ASTM D638 |
| 23°C | 13400 | MPa | ISO 527-2 |
| 100°C | 10800 | MPa | ISO 527-2 |
| 150°C | 6700 | MPa | ISO 527-2 |
| 175°C | 4300 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Fracture, 23°C | 233 | MPa | ISO 527-2 |
| Fracture, 100°C | 148 | MPa | ISO 527-2 |
| Fracture, 150°C | 80.0 | MPa | ISO 527-2 |
| Fracture, 175°C | 72.0 | MPa | ISO 527-2 |
| -- | 221 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Fracture | 2.5 | % | ASTM D638 |
| Fracture, 23°C | 2.5 | % | ISO 527-2 |
| Fracture, 100°C | 2.9 | % | ISO 527-2 |
| Fracture, 150°C | 8.7 | % | ISO 527-2 |
| Fracture, 175°C | 8.5 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 11400 | MPa | ASTM D790 |
| 23°C | 11600 | MPa | ISO 178 |
| 100°C | 9800 | MPa | ISO 178 |
| 150°C | 4000 | MPa | ISO 178 |
| 175°C | 3600 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 317 | MPa | ASTM D790 |
| 23°C | 319 | MPa | ISO 178 |
| 100°C | 227 | MPa | ISO 178 |
| 150°C | 93.0 | MPa | ISO 178 |
| 175°C | 80.0 | MPa | ISO 178 |
| Compressive Strength | 185 | MPa | ASTM D695 |
| Shear Strength | 101 | MPa | ASTM D732 |
| Poisson's Ratio | 0.41 | ASTM E132 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 73 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | |||
| -- | 80 | J/m | ASTM D256 |
| 23°C | 8.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| -- | 770 | J/m | ASTM D256 |
| 23°C | 49 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, annealed, 3.20mm | 297 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 280 | °C | ISO 75-2/A |
| 1.8 MPa, annealed, 3.20mm | 285 | °C | ASTM D648 |
| Continuous Use Temperature | ASTM D3045 | ||
| -- 1 | 164 | °C | ASTM D3045 |
| -- 2 | 185 | °C | ASTM D3045 |
| Melting Temperature | 313 | °C | ASTM D570, ISO 11357-3 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : 0 to 100°C | 2.4E-5 | cm/cm/°C | ASTM E831 |
| Flow : 100 to 200°C | 2.7E-5 | cm/cm/°C | ASTM E831 |
| Lateral : 0 to 100°C | 5.5E-5 | cm/cm/°C | ASTM E831 |
| Lateral : 100 to 200°C | 1.1E-4 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.20 mm) | 21 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 60 Hz | 4.40 | ASTM D150 | |
| 1 MHz | 4.20 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 60 Hz | 5.0E-3 | ASTM D150 | |
| 1 MHz | 0.017 | ASTM D150 | |
| Arc Resistance | 140 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 550 | V | UL 746 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.045 | % | |
| Rear Temperature | 304 - 318 | °C | |
| Front Temperature | 316 - 329 | °C | |
| Processing (Melt) Temp | 321 - 343 | °C | |
| Mold Temperature | 135 | °C |
| Injection instructions |
|---|
| Storage: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Amodel® processing guide. |
| Note Message | |
|---|---|
| 1 . | 20000 hours |
| 2 . | 5000 hours |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUSTAMID 6G GK | Röchling Sustaplast SE & Co. KG | Nylon 6 | SUSTAMID |
| Weatherflex™ CS1525WX NTL01B | Colorite Polymers | PVC, Flexible | Weatherflex™ |
| ALTECH® PA66 C 1000/100 | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| IDI STC 1246 | IDI Composites International | Polyester, TS | IDI STC |
| LNP™ LUBRICOMP™ MX06404 compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ LUBRICOMP™ |