XENOY™ 1102 resin
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | XENOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ngkuSQ_XENOY1102resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unreinforced PC/polyester alloy. Excellent low temperatue impact/chemical resistance to automotive fluids. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.20 | g/cm³ | ASTM D792 |
| -- | 1.19 | g/cm³ | ISO 1183 |
| Specific Volume | 0.830 | cm³/g | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 6.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 0.80 - 1.0 | % | Internal method |
| Transverse flow : 3.20mm | 0.80 - 1.0 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 54.5 | MPa | ASTM D638 |
| Yield | 50.0 | MPa | ISO 527-2/50 |
| Fracture | 45.0 | MPa | ISO 527-2/50 |
| Tensile Strain | |||
| Yield | 4.5 | % | ISO 527-2/50 |
| Fracture 2 | 150 | % | ASTM D638 |
| Fracture | 120 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 3 | 1970 | MPa | ASTM D790 |
| -- 4 | 1880 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 72.0 | MPa | ISO 178 |
| Yield, 50.0mm span 5 | 82.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -30°C | 640 | J/m | ASTM D256 |
| 0°C | 690 | J/m | ASTM D256 |
| 23°C | 800 | J/m | ASTM D256 |
| -30°C 6 | 44 | kJ/m² | ISO 180/1A |
| 0°C 7 | 52 | kJ/m² | ISO 180/1A |
| 23°C 8 | 51 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 6.40mm | 110 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 9 | 103 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 6.40mm | 90.6 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 10 | 79.4 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 50 - 80 | % | |
| Rear Temperature | 243 - 266 | °C | |
| Middle Temperature | 249 - 271 | °C | |
| Front Temperature | 254 - 277 | °C | |
| Nozzle Temperature | 254 - 271 | °C | |
| Processing (Melt) Temp | 260 - 277 | °C | |
| Mold Temperature | 65.6 - 87.8 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 50 - 80 | rpm | |
| Vent Depth | 0.013 - 0.020 | mm |
| Note Message | |
|---|---|
| 1 . | Type 1, 50mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8200-93UV Clear 8390 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Anjacom® 500G | Almaak International GmbH | ABS | Anjacom® |
| DuraFlex 202-6 | Evermore Chemical Industry Co., Ltd. | TPU-Polyether | DuraFlex |
| Polyrocks EP8400X105V-2 | Polyrocks Chemical Co., Ltd | XLPE | Polyrocks |
| RONFALIN® ABS 1541 | A. Schulman Europe | ABS | RONFALIN® |