LNP™ THERMOCOMP™ PF00ASXS compound
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ngdhLX_LNPTHERMOCOMPPF00ASXScompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* PF00ASXS is a compound based on Nylon 6 resin containing Glass Fiber. Added features of this material include: Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound PF-100-10 HS Product reorder name: PF00ASXS |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.57 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.10 - 0.30 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.60 - 0.70 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.60 - 0.80 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.10 - 0.30 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.83 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.97 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 17100 | MPa | ASTM D638 |
| -- | 17300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 214 | MPa | ASTM D638 |
| Fracture | 241 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 2.8 | % | ASTM D638 |
| Fracture | 3.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 12300 | MPa | ASTM D790 |
| -- | 12400 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 329 | MPa | ASTM D790 |
| -- | 318 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 180 | J/m | ASTM D256 |
| 23°C 2 | 19 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 95 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 18.3 | J | ASTM D3763 |
| -- | 22.5 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 198 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 210 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 249 - 260 | °C | |
| Middle Temperature | 266 - 277 | °C | |
| Front Temperature | 277 - 288 | °C | |
| Processing (Melt) Temp | 266 - 277 | °C | |
| Mold Temperature | 82.2 - 93.3 | °C | |
| Back Pressure | 0.344 - 0.689 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAC® PA-777E | CHI MEI CORPORATION | ABS | POLYLAC® |
| PRL NY66-G43 | Polymer Resources Ltd. | Nylon 66 | PRL |
| BMC T45HT | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| CYCOLOY™ C7410 resin | SABIC Innovative Plastics Asia Pacific | PC+ABS | CYCOLOY™ |
| Hanwha Total PP RJ700 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |