Infino EM-8240C
| Category: | PPE , Polyphenylene Ether |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ngSaHg_Infino-EM-8240C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MPPE/GF material that is applied to the main frame of banknote sorter |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238, ISO 1133 | ||
| 280°C/10.0 kg | 42 | g/10 min | |
| 300°C/2.16 kg | 10 | g/10 min | |
| Molding Shrinkage | ASTM D955, ISO 2577 | ||
| Flow : 3.20 mm | 0.18 | % | |
| Across Flow : 3.20 mm | 0.25 | % | |
| Ash Content | 24 | % | ISO 3451 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| ESD 1(23°C) | < 0.1 | sec | JIS L1094 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 7000 | MPa | ASTM D638 |
| -- | 6000 | MPa | ISO 527-2/5 |
| Tensile Strength | |||
| Yield 3 | 98.0 | MPa | ASTM D638 |
| Yield | 100 | MPa | ISO 527-2/5 |
| Break 4 | 110 | MPa | ASTM D638 |
| Break | 100 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 5 | 2.5 | % | ASTM D638 |
| Break | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| -- 6 | 9300 | MPa | ASTM D790 |
| -- 7 | 10000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 8 | 120 | MPa | ASTM D790 |
| -- 9 | 150 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 10(23°C) | 48 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 39 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 39 | J/m | ASTM D256 |
| 23°C 11 | 40 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 139 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 4.00 mm | 140 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 132 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 131 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 118 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 12 | 1.0E+4 | ohms | ASTM D257, IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 | °C | |
| Desiccant Dryer | 100 | °C | |
| Drying Time | |||
| -- | 2.0 to 4.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.10 to 0.20 | % | |
| Rear Temperature | 250 to 280 | °C | |
| Middle Temperature | 260 to 300 | °C | |
| Front Temperature | 270 to 320 | °C | |
| Nozzle Temperature | 310 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Pressure | 78.5 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 45 to 80 | rpm |
| Note Message | |
|---|---|
| 1 . | 50% RH |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 5.0 mm/min |
| 6 . | 2.8 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 2.8 mm/min |
| 9 . | 2.0 mm/min |
| 10 . | Thickness: 4 mm |
| 11 . | Thickness: 4 mm |
| 12 . | 23°C, 50% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Texalan® 3 Series 372D | Austin Novel Materials Co. Ltd. | TPU-Polyester | Texalan® 3 Series |
| TOTAL Polypropylene PPR 7238 | TOTAL Refining & Chemicals | PP Random Copolymer | TOTAL Polypropylene |
| WELLAMID Nylon 6000 MX 400 CP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| DESLOY™ DSC901G2 | DESCO Co., Ltd. | PC | DESLOY™ |
| Sylvin 5170-85 White 1412 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |