Ultraform® N 2320 U03 UNC Q600
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultraform® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ng5QbE_Ultraform-N-2320-U03-UNC-Q600.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ultraform N 2320 U03 UNC Q600 is a rapidly freezing UV stabilized general-purpose injection molding grade. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 7.50 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.18 mm | 2.0 | % | |
| Across Flow | 2.1 | % | ISO 294-4 |
| Flow | 2.1 | % | ISO 294-4 |
| Water Absorption | |||
| Saturation | 0.80 | % | ASTM D570 |
| Saturation, 23°C | 0.80 | % | ISO 62 |
| Equilibrium, 50% RH | 0.20 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2600 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 63.0 | MPa | ASTM D638, ISO 527-2 |
| Yield, -40°C | 93.0 | MPa | ISO 527-2 |
| Yield, 80°C | 33.0 | MPa | ISO 527-2 |
| Tensile Elongation (Yield, 23°C) | 9.4 | % | ASTM D638, ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 30 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 1800 | MPa | |
| 1000 hr | 1400 | MPa | |
| Flexural Modulus (23°C) | 4000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 5.0 | kJ/m² | |
| 23°C | 5.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 180 | kJ/m² | |
| 23°C | 200 | kJ/m² | |
| Notched Izod Impact | |||
| -40°C | 60 | J/m | ASTM D256 |
| 23°C | 69 | J/m | ASTM D256 |
| 23°C | 6.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 160 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 110 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 95.0 | °C | ISO 75-2/A |
| Peak Melting Temperature | 166 | °C | ASTM D3418, ISO 3146 |
| CLTE - Flow | |||
| -- | 6.0E-5 | cm/cm/°C | ASTM E831 |
| -- | 1.1E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V875 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Cri-Line LC-715-75-THK | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| DOWLEX™ 2377 | The Dow Chemical Company | LLDPE | DOWLEX™ |
| DOWLEX™ 2645.01G | The Dow Chemical Company | LLDPE | DOWLEX™ |
| LNP™ THERMOTUF™ VF004S compound | SABIC Innovative Plastics | Nylon, Unspecified | LNP™ THERMOTUF™ |