Elastollan® C 70 A 10 P 000
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | BASF Polyurethanes GmbH |
| Trademark: | Elastollan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nfin9T_Elastollan-C-70-A-10-P-000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Thermoplastic Polyester-Polyurethane with excellent mechanical properties and chemical resistance, outstanding wear resistance, high tear and tensile strength, good damping characteristic and high resilience performance. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.16 | g/cm³ | ISO 1183/A |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 3 sec) | 70 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Loss | 35.0 | mm³ | ISO 4649-A |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Head Temperature | 165 - 185 | °C |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 40.0 | MPa | DIN 53504-S2 |
| Tensile Elongation (Break) | 780 | % | DIN 53504-S2 |
| Tear Strength 1 | 44 | kN/m | ISO 34-1 |
| Additional Information |
|---|
| The plaques are manufactured by injection moulding from pre-dried granules (water content less 0,02%). Test paques are aged 20 hrs at 100°C.Specimens are cut from test plaques. The test conditions: 23°C ± 2°C and 50% ± 6% rel. humidity. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40.0 | °C | |
| Rear Temperature | 170 - 190 | °C | |
| Middle Temperature | 180 - 210 | °C | |
| Front Temperature | 200 - 215 | °C | |
| Nozzle Temperature | 205 - 220 | °C | |
| Processing (Melt) Temp | 205 - 220 | °C | |
| Mold Temperature | 20.0 - 40.0 | °C | |
| Injection Rate | Slow | ||
| Back Pressure | 5.00 - 15.0 | MPa |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Cylinder Zone 1 Temp. | 150 - 170 | °C | |
| Cylinder Zone 2 Temp. | 160 - 180 | °C | |
| Cylinder Zone 3 Temp. | 165 - 185 | °C | |
| Cylinder Zone 4 Temp. | 165 - 185 | °C | |
| Adapter Temperature | 165 - 185 | °C | |
| Die Temperature | 165 - 185 | °C |
| Note Message | |
|---|---|
| 1 . | Method B, right-angle specimen (cut) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 399 X 137783 B | RTP Company | PC | RTP |
| RTP 800 AR 15 TFE 15 | RTP Company | Acetal (POM) Copolymer | RTP |
| CYCOLAC™ INP576 resin | SABIC Innovative Plastics | ABS+SAN | CYCOLAC™ |
| Generic Nylon 6I/6T - Glass Fiber | Generic | Nylon 6I/6T | Generic |
| Iupilon® ECF2010R | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |