EL-Lene™ H5480S
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | SCG Chemicals Co., Ltd. |
| Trademark: | EL-Lene™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nfFkpr_EL-Lene-H5480S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EL-Lene H5480S is a high density polyethylene resin which is suitable for producing monofilament or flat yarn products. It is manufacturered by extrusion process with spinnerette die, T-die, annular die, coathanger die, etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.954 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 25% Igepal, Compression Molded, F50) | 30.0 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 65 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 26.5 | MPa | ASTM D638 |
| Fracture | 38.2 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 1200 | % | ASTM D638 |
| Flexural Modulus | 981 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 0°C | 140 | J/m | ASTM D256 |
| 23°C | 170 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -60.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 126 | °C | ASTM D1525 |
| Melting Temperature | 131 | °C | ASTM D2117 |
| Extrusion instructions |
|---|
| Monofilament Processing-Melt temperature range: 250 to 280°CStretching Temperature: 96 to 100°CStretching Ratio: 8 to12Flat yarn Processing -Melt temperature range: 190 to 260°CStretching Temperature: 100 to 130°CStretching Ratio: 5 to 7 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mapex AT0320GB | Ginar Technology Co., LTD. | Nylon 66 | Mapex |
| StarTUFF TF 75-LR-1 | STAR Thermoplastic Alloys & Rubbers, Inc. | TPE | StarTUFF |
| Staramide PK005EI2 | Eurostar Engineering Plastics | Nylon 6 | Staramide |
| Andur 1-83 AP/Curene® 442 | Anderson Development Company | PUR-Ether/TDI | Andur |
| Sylvin 5175-92 White 1479 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |