| Aegis® H73ZP is a low viscosity nylon 6 extrusion grade homopolymer for cast or blown film. It conforms to FDA requirements of 21 CFR 177.1500 as well as EU Directive 2002/72/EC. It possesses the combination of strength, toughness and thermoforming properties associated with nylon 6 as well as excellent heat, chemical, and abrasion resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (235°C/1.0 kg) | 4.5 | g/10 min | ASTM D1238 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 1.6 | % | ASTM D570 |
| Saturation | 9.5 | % | ASTM D570 |
| Balance | 2.7 | % | ASTM D570 |
| Moisture Content | > 800 | ppm | ASTM D6869 |
| Relative viscosity- @ 96% Sulfuric Acid | 3.01 | ||
| Viscosity- FAV | 73.0 | ASTM D789 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 23°C | 590 | N | ASTM D1922 |
| TD : 23°C | 530 | N | ASTM D1922 |
| Graves Tear | ASTM D1004 | ||
| MD : 23°C | 3530 | N | ASTM D1004 |
| TD : 23°C | 3290 | N | ASTM D1004 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Puncture Index (23°C) 1 | 193.4 | kN/m | |
| Puncture Resistance (23°C) 2 | 1000 | g |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Elastic Modulus - MD 3 | 710 | MPa | ASTM D882 |
| Elastic Modulus - TD 4 | 620 | MPa | ASTM D882 |
| Tensile Strength 5 | ASTM D882 | ||
| MD : Yield | 40.0 | MPa | ASTM D882 |
| TD : Yield | 30.0 | MPa | ASTM D882 |
| MD : Fracture | 90.0 | MPa | ASTM D882 |
| TD : Fracture | 90.0 | MPa | ASTM D882 |
| Tensile Elongation 6 | ASTM D882 | ||
| MD : Fracture | 340 | % | ASTM D882 |
| TD : Fracture | 360 | % | ASTM D882 |
| Carbon Dioxide Transmission Rate (23°C) | 72.8 | cm³/m²/24 hr | ASTM D1434 |
| Nitrogen Transmission Rate (23°C) | 14.0 | cm³/m²/24 hr | ASTM D1434 |
| Oxygen Transmission Rate (23°C) | 40 | cm³/m²/24 hr | ASTM D3985 |
| Water Vapor Transmission Rate (38°C, 100% RH) | 990 | g·mm/m²/atm/24 hr | ASTM F1249 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Melting Temperature | 220 | °C |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| FAV, ASTM D789: 7396% SAV: 3Extractable Content: <.8 sp gr 23/ 23°C using ASTM D792 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.080 | % | |
| Cylinder Zone 1 Temp. | 230 - 260 | °C | |
| Cylinder Zone 2 Temp. | 230 - 260 | °C | |
| Cylinder Zone 3 Temp. | 230 - 260 | °C | |
| Cylinder Zone 4 Temp. | 230 - 260 | °C | |
| Cylinder Zone 5 Temp. | 230 - 260 | °C | |
| Adapter Temperature | 260 - 266 | °C | |
| Melt Temperature | 260 - 270 | °C | |
| Die Temperature | 260 | °C |
| Extrusion instructions |
|---|
| The values listed above in Extrusion are for cast film.Typical Barrel Profile for Tubular (Blown) Films: Barrel Temperature: 246 to 254°C (474 to 490°F) Adapter Temperature: 260°C (500°F) Die Temperature: 254°C (490°F) Processing Melt Temperature: 254 to 260°C (490 to 500°F) Screw Parameters: Metering section: 40% Transition section: 3 to 4 flights Feed section balance of screw length Compression ratio: 3.5:1 to 4.0:1 L/D ratio: 24:1 |
| Note Message | |
|---|---|
| 1 . | ASTM D1306 |
| 2 . | ASTM D1306 |
| 3 . | 23°C |
| 4 . | 23°C |
| 5 . | 23°C |
| 6 . | 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4089 | RTP Company | PPA | RTP |
| Braskem PP H 606 | Braskem | PP Homopolymer | Braskem PP |
| Hypro® PP- CP 35/1.5C | Entec Polymers | PP Impact Copolymer | Hypro® |
| RELENE® F46003E | Reliance Industries Limited | HDPE | RELENE® |
| LNP™ LUBRICOMP™ DP003 compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |