Eleme BFY00919
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Eleme Petrochemical Company Ltd |
| Trademark: | Eleme |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ndkBwH_Eleme-BFY00919.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| With slip & antiblock. Suitable for heavy duty firms for industrial liners, general purpose film, liquid packaging, lamination film etc. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.919 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.90 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Secant Modulus | ASTM D882 | ||
| MD : 25 µm | 220 | MPa | |
| TD : 25 µm | 245 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm | 11.0 | MPa | |
| TD : Yield, 25 µm | 11.0 | MPa | |
| MD : Break, 25 µm | 38.0 | MPa | |
| TD : Break, 25 µm | 34.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm | 800 | % | |
| TD : Break, 25 µm | 900 | % | |
| Dart Drop Impact 1(25 µm) | 3.5 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 5.0 | g | |
| TD : 25 µm | 8.0 | g |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 98.0 | °C | ASTM D1525 2 |
| Note Message | |
|---|---|
| 1 . | F50, 3.8 cm dart, 66 cm drop height |
| 2 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WELLAMID Nylon 6000/52 GV 15 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| Daelim Po1y® PP-173S | DAELIM INDUSTRIAL CO., LTD. | PP Homopolymer | Daelim Po1y® |
| Infino HI-1001BP | SAMSUNG SDI CO., LTD. | PC+ABS | Infino |
| MAJORIS DEG368X - 8432 | AD majoris | PP, Unspecified | MAJORIS |
| Plasmer 5045N/1002 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |