LAMIGAMID® 314
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Schwartz Technical Plastic |
| Trademark: | LAMIGAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ncnQXM_LAMIGAMID-314.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.16 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 2.2 | -- | % | ISO 62 |
| Saturated, 23°C | 7.0 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 160 | 130 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3500 | 2800 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | |||
| Yield | 80.0 | 60.0 | MPa | ISO 527-2 |
| Fracture | 130 | 50.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 20 | -- | % | ISO 527-2 |
| Flexural Modulus | 3400 | 2500 | MPa | ISO 178 |
| Compressive Stress | ISO 604 | |||
| 20% strain | 95.0 | -- | MPa | ISO 604 |
| 10% strain | 68.0 | -- | MPa | ISO 604 |
| 5% strain | 42.0 | -- | MPa | ISO 604 |
| Coefficient of Friction | ASTM D1894 | |||
| With steel-dynamic | 0.040 | 0.080 | ASTM D1894 | |
| With steel-static | 0.31 | -- | ASTM D1894 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | > 2.7 | > 12 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength | No Break | No Break | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 210 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 120 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | -- | °C | ISO 3146 |
| CLTE - Flow (20 to 100°C) | 7.0E-5 - 8.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 1670 | -- | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 0.25 | -- | W/m/K | ISO 8302 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Dielectric Strength | 50 | 20 | kV/mm | IEC 60243-1 |
| Dielectric Constant | 3.70 | -- | IEC 60250 | |
| Dissipation Factor | 0.030 | -- | IEC 60250 |
| Additional Information |
|---|
| 干燥 Creep Rate Stress, DIN 53444, 1% Elongation: >15 N/mm²Creep Rate Stress, DIN 53444, 2% Elongation: >20 N/mm²Friction Wear: 0.10 µm/KmPenetration Resistance, DIN 53482: 1E15 ohm-cmCreepage/leakage Resistance: KA3cThermal Expension: 0.1 %/10°CSafe Temperature Range, short periods: 180°CSafe Temperature Range, permanent: -40°C |
| 调节后的 Creep Rate Stress, DIN 53444, 1% Elongation: >8 N/mm²Creep Rate Stress, DIN 53444, 2% Elongation: >12 N/mm²Friction Wear: 0.10 µm/KmPenetration Resistance, DIN 53482: 1E12 ohm-cmCreepage/leakage Resistance: KA3bThermal Expension: 0.1 %/10°CSafe Temperature Range, short periods: 180°CSafe Temperature Range, permanent: 120°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPE ML-1533N | Teknor Apex Company | TPE | Sarlink® TPE |
| SUNPRENE® FA70HH | Mitsubishi Chemical Performance Polymers, Inc. | PVC Elastomer | SUNPRENE® |
| COSMOLEX® FS253R | TPC, The Polyolefin Company (Singapore) Pte Ltd | LLDPE | COSMOLEX® |
| ExxonMobil™ LDPE LD 258 | ExxonMobil Chemical | LDPE | ExxonMobil™ LDPE |
| Elastocon® STK56PA | Elastocon TPE Technologies | TPE | Elastocon® |