EL-Pro™ P852J
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | SCG Chemicals Co., Ltd. |
| Trademark: | EL-Pro™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nce2TR_EL-Pro-P852J.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EL-Pro P852J is a random copolymer polypropylene resin which has high flowability, high clarity and contains anti-static agent suitable for injection molding process. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 35 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | Internal Method | ||
| -- 1 | 1.3 | % | |
| -- 2 | 1.4 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 80 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 3 | ASTM D638 | ||
| Yield | 29.4 | MPa | |
| Break | 17.7 | MPa | |
| Tensile Elongation 4(Break) | 600 | % | ASTM D638 |
| Flexural Modulus | 1230 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 0°C | 34 | J/m | |
| 23°C | 54 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Annealed 5 | 90.0 | °C | |
| 1.8 MPa, Annealed 6 | 50.0 | °C | |
| Brittleness Temperature | -20.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 130 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | 80 | ASTM D2457 | |
| Haze | 12 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Temperature | 150 | °C | ASTM D2117 |
| Note Message | |
|---|---|
| 1 . | 2mmt. TD |
| 2 . | 2mmt, MD |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 4.6 kg/cm^2 |
| 6 . | 18.5 kg/cm^2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 3400-G-640 | RTP Company | LCP | RTP |
| SOLPLAST TC 3000B | UTEKSOL d.o.o. | SBS | SOLPLAST TC |
| Kumho KBR 01L | Korea Kumho Petrochemical Co., Ltd. | PBR, High Cis | Kumho KBR |
| Plenco 07500 (Transfer) | Plastics Engineering Co. | Phenolic | Plenco |
| LNP™ STAT-KON™ ZE0039 compound | SABIC Innovative Plastics | Polyphenylene, Unspecified | LNP™ STAT-KON™ |