REPOL® H350EG
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Reliance Industries Limited |
| Trademark: | REPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ncUYRI_REPOL-H350EG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Repol H350EG is recommended for use in Extrusion Coating/Lamination process. Repol H350EG is an ideal material for coating of polypropylene woven fabrics. Repol H350EG is designed to provide excellent flow characteristics, low neck-in & consistent processability, good surface finish & gloss and excellent adhesion to substrate. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 38 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, Injection Molded) | 34.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Yield, Injection Molded) | 9.0 | % | ASTM D638 |
| Flexural Modulus - 1% Secant (Injection Molded) | 1500 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, Injection Molded) | 24 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 104 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type I, 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unichem 7588 | Colorite Polymers | PVC, Unspecified | Unichem |
| Generic PEEK - Nano, Carbon | Generic | PEEK | Generic |
| INSPIRE™ TF2301 ESU | Trinseo | PP, Unspecified | INSPIRE™ |
| LGG 104 | LG Polymers India Pvt. Ltd. | PS (GPPS) | LGG |
| PENTAMID B GV30 H RC schwarz | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |