INEOS LLDPE LL6808AA
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | INEOS Olefins & Polymers Europe |
| Trademark: | INEOS LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ncQzse_INEOSLLDPELL6808AA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LL6808AA is a linear low density polyethylene copolymer containing hexene-1 as co-monomer formulated with antioxidants. Benefits & Features LL6808AA offers the following properties:
Applications LL6808AA is a low-gel polymer designed for:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.932 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.85 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 2.5 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| 1% secant, MD : 25 µm, blown film | 290 | MPa | ISO 527-3 |
| 1% secant, TD : 25 µm, blown film | 305 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 25 µm, blown film | 59.0 | MPa | ISO 527-3 |
| TD : Yield, 25 µm, blown film | 44.0 | MPa | ISO 527-3 |
| MD : Broken, 25 µm, blown film | 15.0 | MPa | ISO 527-3 |
| TD : Broken, 25 µm, blown film | 14.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 25 µm, blown film | 720 | % | ISO 527-3 |
| TD : Broken, 25 µm, blown film | 810 | % | ISO 527-3 |
| Dart Drop Impact (25 µm, Blown Film) | 110 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, blown film | 150 | g | ASTM D1922 |
| TD : 25 µm, blown film | 560 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 110 | °C | ISO 306/A50 |
| Peak Melting Temperature 1 | 127 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm, Blown Film) | 63 | ASTM D2457 | |
| Haze (25.0 µm, Blown Film) | 5.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 - 230 | °C |
| Note Message | |
|---|---|
| 1 . | 2nd heating |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren M2500CD (Premium-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| Telcar® SGI50010 | Teknor Apex Asia Pacific PTE. LTD. | TPE | Telcar® |
| Terralene® WF 3516 | FKuR Kunststoff GmbH | HDPE | Terralene® |
| Chemlon® AT10 | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| MAJORIS DW305 - 8090 | AD majoris | PP, Unspecified | MAJORIS |