LNP* STAT-KON* AE003 is a compound based on ABS containing 15% Carbon Fiber. Added feature of this grade is: Electrically Conductive. Also known as: LNP* STAT-KON* Compound AC-1003 Product reorder name: AE003 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 0.10 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.55 | % | ASTM D955 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.19 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.28 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 12800 | MPa | ASTM D638 |
| -- | 11500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture 2 | 92.0 | MPa | ASTM D638 |
| Fracture | 93.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture 3 | 0.90 | % | ASTM D638 |
| Fracture | 0.90 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 4 | 12600 | MPa | ASTM D790 |
| -- 5 | 12300 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 119 | MPa | ISO 178 |
| Yield, 50.0mm span 6 | 114 | MPa | ASTM D790 |
| Fracture, 50.0mm span 7 | 95.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 60 | J/m | ASTM D256 |
| 23°C 8 | 5.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 270 | J/m | ASTM D4812 |
| 23°C 9 | 16 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 7.10 | J | ASTM D3763 |
| -- | 2.18 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 105 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 10 | 104 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 102 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 11 | 104 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM D696 | ||
| Flow : -30 to 30°C | 1.9E-5 | cm/cm/°C | ASTM D696 |
| Lateral : -30 to 30°C | 6.6E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0 - 4.0 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 - 0.10 | % | |
| Rear Temperature | 204 - 216 | °C | |
| Middle Temperature | 232 - 243 | °C | |
| Front Temperature | 266 - 277 | °C | |
| Processing (Melt) Temp | 260 | °C | |
| Mold Temperature | 71.1 - 82.2 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Greene 209 | Greene, Tweed & Co. | NBR | Greene |
| Optimum® 2000 | RAUH Polymers, Inc. | Copolyester | Optimum® |
| Polychim HV22XF | Polychim Industrie S.A.S. | PP Homopolymer | Polychim |
| Sylvin 9077-70 Grey 9516 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| RONFALIN® ABS 1352 A | A. Schulman Europe | ABS | RONFALIN® |