GELOY™ HRA170D resin
| Category: | ASA+PC , Acrylonitrile Styrene Acrylate + PC |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | GELOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nbt0gr_GELOY-HRA170D-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GELOY HRA170D resin is a PC-ASA blend with permanent antistatic behavior. It is typically used in applications that require antidust properties and high impact retention. GELOY HRA170D resin is typically used in various outdoor and indoor applications requiring superior heat aging properties and colour stability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 220°C/10.0 kg | 8.5 | g/10 min | ASTM D1238 |
| 260°C/5.0 kg | 30 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 8.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 220°C/10.0 kg | 8.00 | cm³/10min | |
| 260°C/5.0 kg | 29.0 | cm³/10min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 57 | ISO 2039-2 | |
| Shore Hardness (Shore D) | 77 | ISO 868 | |
| Ball Indentation Hardness (H 358/30) | 63.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2160 | MPa | ASTM D638 |
| -- | 2150 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 50.0 | MPa | ASTM D638 |
| Yield 3 | 54.0 | MPa | ASTM D638 |
| Yield | 51.0 | MPa | ISO 527-2/5 |
| Yield | 54.0 | MPa | ISO 527-2/50 |
| Break 4 | 58.0 | MPa | ASTM D638 |
| Break 5 | 59.0 | MPa | ASTM D638 |
| Break | 65.0 | MPa | ISO 527-2/5 |
| Break | 58.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 6 | 5.0 | % | ASTM D638 |
| Yield 7 | 5.0 | % | ASTM D638 |
| Yield | 130 | % | ISO 527-2/5 |
| Yield | 5.0 | % | ISO 527-2/50 |
| Break 8 | 160 | % | ASTM D638 |
| Break 9 | 140 | % | ASTM D638 |
| Break | 130 | % | ISO 527-2/50 |
| Flexural Modulus 10 | 2100 | MPa | ISO 178 |
| Flexural Stress | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 11 | ISO 179/1eA | ||
| -30°C | 17 | kJ/m² | |
| 23°C | 45 | kJ/m² | |
| Notched Izod Impact | |||
| -30°C | 140 | J/m | ASTM D256 |
| 23°C | 450 | J/m | ASTM D256 |
| -30°C 12 | 14 | kJ/m² | ISO 180/1A |
| 23°C 13 | 45 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 64.0 mm Span 14 | 127 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 106 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 15 | 104 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 137 | °C | ISO 306/A50 |
| -- | 138 | °C | ISO 306/A120 |
| -- | 121 | °C | ISO 306/B50 |
| -- | 122 | °C | ISO 306/B120 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 95.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Suggested Shot Size | 40 to 80 | % | |
| Rear Temperature | 230 to 250 | °C | |
| Middle Temperature | 235 to 255 | °C | |
| Front Temperature | 245 to 260 | °C | |
| Nozzle Temperature | 235 to 255 | °C | |
| Processing (Melt) Temp | 255 to 270 | °C | |
| Mold Temperature | 60.0 to 85.0 | °C | |
| Back Pressure | 0.300 to 1.00 | MPa | |
| Screw Speed | 30 to 80 | rpm | |
| Vent Depth | 0.038 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | Type I, 5.0 mm/min |
| 7 . | Type I, 50 mm/min |
| 8 . | Type I, 5.0 mm/min |
| 9 . | Type I, 50 mm/min |
| 10 . | 2.0 mm/min |
| 11 . | 80*10*4 sp=62mm |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 mm |
| 15 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tarnamid® T- 27 GF40 FRV0 | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| APEX® 93-A0591C-97 | Teknor Apex Company | PVC, Flexible | APEX® |
| Hapflex™ 571-6 | Hapco Inc. | TP, Unspecified | Hapflex™ |
| LONGLITE® TPEE 1163LL | CCP Group | TPEE | LONGLITE® TPEE |
| Lucel® N109WR | LG Chem Ltd. | Acetal (POM) Copolymer | Lucel® |