CALIBRE™ 300-10
| Category: | PC , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CALIBRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nbm8Gt_CALIBRE-300-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CALIBRE™ 300-10 Polycarbonate resins offer exceptional impact resistance, heat distortion resistance, and optical clarity. The CALIBRE 300-10 series products are available in 4 additive packages: CALIBRE 300: No mold release or UV Stabilizer. CALIBRE 301: Mold release. CALIBRE 302: UV stabilizer. CALIBRE 303: Mold release and UV stabilizer Govt. and Industry Standards:
Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.20 | g/cm³ | ASTM D792, ISO 1183/A |
| -- | 1200 | kg/m³ | ISO 1183 1 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238, ISO 1133 |
| Melt volume-flow rate (300°C/1.2 kg) | 8.00 | cm³/10min | ISO 1133 2 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955, ISO 294-4 |
| Water Absorption | ASTM D570, ISO 62 | ||
| 23°C, 24 hr | 0.15 | % | |
| Equilibrium, 23°C, 50% RH | 0.32 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 73 | ||
| R-Scale | 118 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 3 | 2410 | MPa | ASTM D638 |
| -- | 2300 | MPa | ISO 527-2/50, ISO 527-2 4 |
| Tensile Strength | |||
| Yield 5 | 60.0 | MPa | ASTM D638 |
| Yield | 60.0 | MPa | ISO 527-2/50, ISO 527-2 6 |
| Break 7 | 71.0 | MPa | ASTM D638 |
| Break | 71.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 8 | 6.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/50, ISO 527-2 9 |
| Break 10 | 150 | % | ASTM D638 |
| Break | 150 | % | ISO 527-2/50 |
| Nominal strain at break | > 50 | % | ISO 527-2 11 |
| Flexural Modulus | |||
| -- 12 | 2410 | MPa | ASTM D790 |
| -- 13 | 2400 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 14 | 96.5 | MPa | ASTM D790 |
| -- 15 | 97.0 | MPa | ISO 178 |
| Taber Abrasion Resistance | 45 | % | ASTM D1044 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Average Extent of Burning | 3 | cm | ASTM D635 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23°C | 35 | kJ/m² | ISO 179/1eA |
| -30°C | 13.0 | kJ/m² | ISO 179/1eA 16 |
| 23°C | 90.0 | kJ/m² | ISO 179/1eA 17 |
| Charpy impact strength | ISO 179/1eU 18 | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact | |||
| 23°C | 910 | J/m | ASTM D256 |
| 23°C | 90 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact (23°C) | No Break | ASTM D256, ISO 180 | |
| Instrumented Dart Impact 19(23°C, Total Energy) | 87.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Annealed | 144 | °C | ASTM D648, ISO 75-2/B |
| 0.45 MPa | 145 | °C | ISO 75-2 20 |
| 1.8 MPa, Unannealed | 128 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 125 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed | 141 | °C | ASTM D648, ISO 75-2/A |
| 1.8 MPa | 131 | °C | ISO 75-2 21 |
| Vicat Softening Temperature | |||
| -- | 149 | °C | ASTM D1525, ISO 306/B50 8 22 |
| 50°C/h, B (50N) | 149 | °C | ISO 306 23 |
| Ball Indentation Temperature | 125 | °C | IEC 60335-1 |
| CLTE - Flow | |||
| -40 to 82°C | 6.8E-5 | cm/cm/°C | ASTM D696 |
| -- | 7.0E-5 | cm/cm/°C | ISO 11359-2 24 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | |||
| -- | 2.0E+17 | ohms·cm | ASTM D257 |
| -- | > 1.0E+13 | ohms·m | IEC 60093 25 |
| Dielectric Strength | 17 | kV/mm | ASTM D149, IEC 60243-1 |
| Dielectric Constant | |||
| 60 Hz | 3.00 | ASTM D150 | |
| 1 MHz | 3.00 | ASTM D150, IEC 60250 26 | |
| 100 Hz | 3.00 | IEC 60250 27 | |
| Dissipation Factor | |||
| 50 Hz | 1.0E-3 | ASTM D150 | |
| 1 MHz | 2.0E-3 | ASTM D150, IEC 60250 28 | |
| 100 Hz | 1.0E-3 | IEC 60250 29 | |
| Comparative Tracking Index (2.00 mm, Solution A) | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 30 | UL 94 | ||
| 1.59 mm | HB | ||
| 3.20 mm | HB | ||
| Burning Behav. at 1.6mm nom. thickn. (1.60 mm, UL) | HB | ISO 1210 31 | |
| Burning Behav. at thickness h (3.20 mm, UL) | HB | ISO 1210 32 | |
| Oxygen Index 33 | 26 | % | ISO 4589-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.586 | ASTM D542, ISO 489 | |
| Transmittance | 89.0 | % | ASTM D1003 |
| Haze | 1.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | 51 mm/min |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | 51 mm/min |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | 51 mm/min |
| 8 . | 51 mm/min |
| 9 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 10 . | 51 mm/min |
| 11 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 12 . | Method I (3 point load), 2.0 mm/min |
| 13 . | 2.0 mm/min |
| 14 . | Method I (3 point load), 2.0 mm/min |
| 15 . | 2.0 mm/min |
| 16 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 17 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 18 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 19 . | 3.39 m/sec |
| 20 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 21 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 22 . | Rate A (50°C/h), Loading 2 (50 N) |
| 23 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 24 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 25 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 26 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 27 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 28 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 29 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 30 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 31 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 32 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 33 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro PP-CO-20GF | Pro Polymers | PP Copolymer | Pro-Comp™ |
| S&E Automotive XP23-45 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E Automotive |
| TOTAL Polypropylene PPC 12712 | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| Zytel® RS LC4601 NC010 | DuPont Performance Polymers | Nylon, Unspecified | Zytel® RS |
| Sylvin 2900-75 Clear 8391 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |