TOTAL Polyethylene HDPE HL 535
| Category: | HDPE, MMW , High Density (MMW) Polyethylene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | naldFr_TOTAL-Polyethylene-HDPE-HL-535.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TOTAL Polyethylene HL 535 is a High Density (MMW) Polyethylene material. It is available in North America for coextrusion. Important attributes of TOTAL Polyethylene HL 535 are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.955 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.35 | g/10 min | |
| 190°C/21.6 kg | 30 | g/10 min |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus 1 | ASTM D882A | ||
| 1% Secant, MD : 25 µm, Blown Film | 917 | MPa | |
| 1% Secant, TD : 25 µm, Blown Film | 1280 | MPa | |
| Tensile Strength 2 | ASTM D882A | ||
| MD : Yield, 25 µm, Blown Film | 27.6 | MPa | |
| TD : Yield, 25 µm, Blown Film | 29.6 | MPa | |
| MD : Break, 25 µm, Blown Film | 43.4 | MPa | |
| TD : Break, 25 µm, Blown Film | 29.6 | MPa | |
| Tensile Elongation 3 | ASTM D882A | ||
| MD : Break, 25 µm, Blown Film | 500 | % | |
| TD : Break, 25 µm, Blown Film | 25 | % | |
| Dart Drop Impact (25 µm, Blown Film) | < 50 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, Blown Film | 8.0 | g | |
| TD : 25 µm, Blown Film | 1100 | g | |
| Water Vapor Transmission Rate (38°C, 25 µm, Blown Film) | 11 | g/m²/24 hr | ASTM F1249 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 132 | °C | ASTM D3418 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 193 to 216 | °C |
| Note Message | |
|---|---|
| 1 . | 25 mm/min |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| APEX® RM 8202 | Teknor Apex Company | PVC, Rigid | APEX® |
| Globalprene® 3522 | Lee Chang Yung Chemical Industry Corp. | SBS | Globalprene® |
| Jamplast ASA Ex-01 | Jamplast, Inc. | ASA | Jamplast |
| LNP™ LUBRICOMP™ Cycoloy_C2801 compound | SABIC Innovative Plastics | PC+ABS | LNP™ LUBRICOMP™ |
| Lucel® GC225 | LG Chem Ltd. | Acetal (POM) Copolymer | Lucel® |