VALOX™ EH7020HF resin
| Category: | PBT+PET , Polybutylene Terephthalate + PET |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nahhGt_VALOXEH7020HFresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| VALOX EH7020HF is a mineral filled PBT/PET that offers good surface appearance, high flow and good heat performance. EH7020HF was developed for automotive bezel application that requires basecoat + top coat metalization. EH7020HF is higher flow version of EH7020. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.49 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 265°C/2.16 kg | 64 | g/10 min | ASTM D1238 |
| 266°C/1.2 kg | 36 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (265°C/2.16 kg) | 52.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 5880 | MPa | ASTM D638 |
| -- | 4800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 56.0 | MPa | ASTM D638 |
| Yield | 45.0 | MPa | ISO 527-2/5 |
| Fracture 3 | 55.0 | MPa | ASTM D638 |
| Fracture | 57.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 2.0 | % | ASTM D638 |
| Yield | 1.5 | % | ISO 527-2/5 |
| Fracture 5 | 2.0 | % | ASTM D638 |
| Fracture | 1.9 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 6 | 4680 | MPa | ASTM D790 |
| -- 7 | 4710 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 96.0 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 93.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 27 | J/m | ASTM D256 |
| 23°C 9 | 2.7 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 70.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span 10 | 77.0 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | 179 | °C | ISO 306/B120 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 80 | % | |
| Rear Temperature | 238 - 254 | °C | |
| Middle Temperature | 243 - 260 | °C | |
| Front Temperature | 249 - 266 | °C | |
| Nozzle Temperature | 243 - 260 | °C | |
| Processing (Melt) Temp | 249 - 266 | °C | |
| Mold Temperature | 65.6 - 87.8 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 50 - 80 | rpm | |
| Vent Depth | 0.025 - 0.038 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Scolefin 13 T 10-0 | Ravago Group | PP Homopolymer | Scolefin |
| TAROPRENE® 2 A55 E1G | Taro Plast S.p.A. | TPV | TAROPRENE® |
| Titacon® AL900 | Titan Plastics Compounds Co., Ltd. | Acetal (POM) Homopolymer | Titacon® |
| Lifocork® UV 701021-2 | ELASTO | TPE | Lifocork® |
| MAJORIS DEG368X - 8432 | AD majoris | PP, Unspecified | MAJORIS |