LUVOCOM® 3/CF/12/EG Datasheet,Nylon 6,Lehmann & Voss & Co.-SHANGHAI SUSHENG

Message
LUVOCOM®3/CF/12/EG is a polyamide 6 (nylon 6) material, which contains a 12% carbon fiber reinforced material. This product is available in Europe, and the processing method is: profile extrusion molding. LUVOCOM®The main features of 3/CF/12/EG are: Conductivity High stiffness high strength high viscosity Electrostatic protection Typical application areas include: engineering/industrial accessories textile/fiber Automotive Industry Handle

General Information
Filler / Reinforcement	Carbon fiber reinforced material, 12% filler by weight
Features	Conductivity Rigidity, high High strength Electrostatic discharge protection Good wear resistance Viscosity, High
Uses	Handle Textile applications Engineering accessories Roller Application in Automobile Field Profile
Appearance	Natural color
Processing Method	Profile extrusion molding

Physical	Nominal Value	Unit	Test Method
Density	1.18	g/cm³	ISO 1183
Molding Shrinkage	0.30 - 0.70	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 1.3	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	7500	MPa	ISO 527-2
Tensile Stress (Break)	140	MPa	ISO 527-2
Tensile Strain (Yield)	3.0	%	ISO 527-2
Flexural Modulus	7000	MPa	ISO 178
Flexural Stress	210	MPa	ISO 178
Coefficient of Friction
Dynamic	0.24
Static	0.20
Flexural Strain at Flexural Strength	4.5	%	ISO 178

Thermal	Nominal Value	Unit	Test Method
Maximum operating temperature- Short Term	130	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance		ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength			ISO 179/1fU
-30°C	45	kJ/m²	ISO 179/1fU
23°C	55	kJ/m²	ISO 179/1fU

Thermal	Nominal Value	Unit	Test Method
Continuous Use Temperature	90.0	°C	UL 746B
Vicat Softening Temperature	210	°C	ISO 306/A
CLTE - Flow	4.0E-5	cm/cm/°C	DIN 53752
Thermal Conductivity	0.33	W/m/K	DIN 52612

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	< 1.0E+5	ohms	IEC 60093

Injection	Nominal Value	Unit
Drying Temperature
A	75.0	°C
B	105	°C
Drying Time
A	10 - 16	hr
B	4.0 - 6.0	hr
Suggested Max Moisture	0.10	%
Rear Temperature	250 - 270	°C
Middle Temperature	270 - 290	°C
Front Temperature	280 - 300	°C
Nozzle Temperature	270 - 280	°C
Processing (Melt) Temp	270	°C
Mold Temperature	70.0 - 110	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water rapidly, originally sealed containers should only be opened immediately before processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water rapidly, originally sealed containers should only be opened immediately before processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Category:	Nylon 6 , Polyamide 6
Manufacturer:	Lehmann & Voss & Co.
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	naUB7k_LUVOCOM-3-CF-12-EG.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
ALCOM® PC 740/4 CC1121-05LD	ALBIS PLASTIC GmbH	PC	ALCOM® PC
HiFill® PA6/6 1550 GF40	Techmer Engineered Solutions	Nylon 66	HiFill®
Kynar Flex® 3121-50	Arkema	PVDF	Kynar Flex®
OpteSTAT™ PBT DP492x1	Ovation Polymers Inc.	PBT	OpteSTAT™
Sylvin 2990-78LG Clear 876	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin