| 40% MINERAL FILLED, HEAT STABILIZIED POLYPROPYLENE FOR INJECTION MOULDING APPLICATIONS. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.80 to 1.2 | % | |
| -- | 0.80 to 1.2 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 20.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2900 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 55.0 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 75 | J/m | ASTM D256 |
| 23°C | 7.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 130 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 75.0 | °C | ASTM D648, ISO 75-2/A |
| Maximum Use Temperature - Short Peaks Operation | 140 | °C | |
| Maximum Continuous Use Temperature | 100 | °C | |
| Melting Temperature | 165 | °C | ISO 11357-3, ASTM D3418 |
| Thermal Conductivity | 140 | W/m/K | ASTM C177, DIN 52612 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 190 to 220 | °C | |
| Middle Temperature | 200 to 225 | °C | |
| Front Temperature | 205 to 230 | °C | |
| Mold Temperature | 30.0 to 65.0 | °C | |
| Injection Pressure | 70.0 to 105 | MPa | |
| Holding Pressure | 35.0 to 70.0 | MPa | |
| Back Pressure | 0.350 to 0.700 | MPa | |
| Screw Speed | 60 to 90 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TC8FLN (Series: FR/AP) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Vyncolit® E 8354-19189-2 | Vyncolit N.V. | Epoxy | Vyncolit® |
| 3M™ Dyneon™ PTFE Compound TF 8615 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| Kingfa FRHIPS-113 | Kingfa | PS (HIPS) | Kingfa |
| Hyundai EP Adhesives RE140R/1002 | HYUNDAI EP Co., Ltd. | PP, Unspecified | Hyundai EP Adhesives |