Order Products : sales@su-jiao.com
CALIBRE鈩?2061-10
| Category: | PC , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CALIBRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nZe6sy_CALIBRE-2061-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CALIBRE™ 2061-10 resin is suitable for steam and ethylene oxide sterilization required by the health care industry. CALIBRE 2061-10 provides exceptional clarity, heat resistance, impact strength, processability, and has low contamination levels. CALIBRE 2061-10 resin is compliant with ISO 10993 (Biological Evaluation of Medical Devices) and is suitable for use in approved medical applications. This product contains mold release. Main Characteristics:
Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2/50 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 60.0 | MPa | |
| Break | 71.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 6.0 | % | |
| Break | 150 | % | |
| Flexural Modulus | 2400 | MPa | ISO 178 |
| Flexural Stress | 97.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 88 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength (23°C) | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Annealed | 144 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 125 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed | 141 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 149 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 3.00 mm | HB | ||
| 0.750 mm | V-2 | ||
| 1.50 mm | V-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 87.0 to 91.0 | % | ASTM D1003 |
| Haze | 0.70 to 1.5 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Axiall PVC 19481 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| ELASTOSIL® RT 426 | Wacker Chemie AG | Silicone | ELASTOSIL® RT |
| POLYFORT® FIPP 20 T LE K1832 | A. Schulman Europe | PP Copolymer | POLYFORT® |
| Hostacom XBR 169 G G31463 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Sylvin 5132-86 Clear Blue 8376 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |