LNP™ THERMOCOMP™ DC006 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nZc4GU_LNP-THERMOCOMP-DC006-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* DC006 is a compound based on Polycarbonate resin containing Carbon Fiber.This product is also known as THERMOCOMP* DC-1006. Also known as: LNP* THERMOCOMP* Compound DC-1006 Product reorder name: DC006 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 0.090 | % | Internal Method |
| Flow : 24 hr | 0.10 to 0.20 | % | ASTM D955 |
| Across Flow | 0.33 | % | Internal Method |
| Across Flow : 24 hr | 0.20 to 0.40 | % | ASTM D955 |
| Water Absorption (24 hr, 50% RH) | 0.12 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 15900 | MPa | ASTM D638 |
| -- | 15800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 141 | MPa | ASTM D638 |
| Yield | 141 | MPa | ISO 527-2/5 |
| Break 3 | 141 | MPa | ASTM D638 |
| Break | 141 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 1.9 | % | ASTM D638 |
| Yield | 1.8 | % | ISO 527-2/5 |
| Break 5 | 1.9 | % | ASTM D638 |
| Break | 1.8 | % | ISO 527-2/5 |
| Flexural Modulus 6 | 14300 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 192 | MPa | ISO 178 |
| Yield, 50.0 mm Span 7 | 195 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 69 | J/m | ASTM D256 |
| 23°C 8 | 6.3 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 590 | J/m | ASTM D4812 |
| 23°C 9 | 44 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 12.0 | J | ASTM D3763 |
| -- | 4.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 147 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 148 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 142 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 143 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 2.4E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 60°C | 4.4E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 1.1E-5 | cm/cm/°C | ASTM E831 |
| Transverse : 23 to 60°C | 2.0E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Polypro™ BJS-MU | Prime Polymer Co., Ltd. | PP Copolymer | Prime Polypro™ |
| Andur M-33 (94% 1,4BD/ 6% TMP) | Anderson Development Company | PUR-Ester/MDI | Andur |
| FHR EPS 54-5354 | Flint Hills Resources, LP | PS (EPS) | FHR EPS |
| Huafon GW-100 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| Lupox® TE5000SZ | LG Chem Ltd. | PC+PBT | Lupox® |