LEXAN™ LUX9610 resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nZUHAX_LEXANLUX9610resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LUX9610 is a UV stabilized flame retardant transparent PC featuring non brominated and non chlorinated FR system with good flow and thin wall FR performance providing good color stability under heat exposure. Developed for lightguide and LED applications. It meets WEEE/RoHS requirements for various applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.20 | g/cm³ | ASTM D792 |
| -- | 1.07 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 6.3 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow 1 | 0.60 - 0.80 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 2 | 2320 | MPa | ASTM D638 |
| Tensile Strength 3 | ASTM D638 | ||
| Yield | 64.0 | MPa | ASTM D638 |
| Fracture | 62.0 | MPa | ASTM D638 |
| Tensile Elongation 4 | ASTM D638 | ||
| Yield | 6.0 | % | ASTM D638 |
| Fracture | 110 | % | ASTM D638 |
| Flexural Modulus 5(50.0 mm Span) | 2330 | MPa | ASTM D790 |
| Flexural Strength 6(Yield, 50.0 mm Span) | 101 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 120 | J/m | ASTM D256 |
| 23°C | 800 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 2100 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 75.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 142 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 138 | °C | ASTM D648 |
| Vicat Softening Temperature | 146 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 95°C | 6.8E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 95°C | 6.8E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | 125 | °C | UL 746 |
| RTI Imp | 115 | °C | UL 746 |
| RTI | 125 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 1 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 260 - 282 | °C | |
| Middle Temperature | 271 - 293 | °C | |
| Front Temperature | 282 - 304 | °C | |
| Nozzle Temperature | 277 - 299 | °C | |
| Processing (Melt) Temp | 282 - 304 | °C | |
| Mold Temperature | 71.1 - 93.3 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 50 mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2800 B-55A FR | RTP Company | TPV | RTP |
| Udel® P-3500 LCD | Solvay Specialty Polymers | PSU | Udel® |
| NuSil MED-1055 | NuSil Technology | Silicone | NuSil |
| HiFill® PA6 0425 | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| INSTRUC PPGF15FC | Infinity LTL Engineered Compounds | PP, Unspecified | INSTRUC |