Lutene® FB0800
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lutene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nYr7qp_Lutene-FB0800.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LUTENE FB0800 is mainly intended for the extrusion of blown film with high mechanical property for the manufacture of greenhouse film. LUTENE FB0800 have the excellent mechanical properties and optical properties make suitable for manufacture of greenhouse films. LUTENE FB0800 contains neither slip agent nor antiblock agent and antiblock agent for agricultural films . Applications: Large width film for greenhouse, Tunnel films. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.921 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | 0.15 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Recommended / Available | 50 to 300 µm | ||
| Tensile Strength | ASTM D882 | ||
| MD : Fracture | 21.7 | MPa | ASTM D882 |
| TD : Fracture | 20.7 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 550 | % | ASTM D882 |
| TD : Fracture | 650 | % | ASTM D882 |
| Dart Drop Impact | 230 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 280 | g | ASTM D1922 |
| TD | 350 | g | ASTM D1922 |
| Oxygen Permeability | 2000 | cm³/m²/24 hr | Internal method |
| Water Vapor Transmission | 12 | g/m²/24 hr | Internal method |
| Nitrogen Permeability | 3500 | cm³/m²/24 hr | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 94.0 | °C | ASTM D1525 1 |
| Melting Temperature | 110 | °C | DSC |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze | 8.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 - 200 | °C |
| Extrusion instructions |
|---|
| Blow up ratio: 1.5 to 3 |
| Note Message | |
|---|---|
| 1 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| polyvic® E-1838-IL TD | Unipack Plasindo | PVC, Unspecified | polyvic® |
| SILVER® F-1 | Guangdong Silver Age Sci & Tech. Co., Ltd | PVC, Unspecified | SILVER® |
| WINTEC™ WMG03 | Japan Polychem Corporation | PP Random Copolymer | WINTEC™ |
| Fiberfil® PP-60/TC/20 | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| Hostacom PC072-3 NATRL | LyondellBasell Industries | PP Homopolymer | Hostacom |