PRE-ELEC® PE 1250
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Premix Oy |
| Trademark: | PRE-ELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nYQGM7_PRE-ELEC-PE-1250.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRE-ELEC® PE 1250 is a conductive thermoplastic concentrate based on PE-HD. Conductivity is achieved by using special conductive carbon black. PRE-ELEC® PE 1250 contains a high load of carbon black and it can be diluted up to 50% with virgin or recycled PE-HD. The actual amount should always be tested as it also depends on the processing conditions. Typical applications for PRE-ELEC® PE 1250 include extruded pipes, profiles and sheets. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.02 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 1.6 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 24.0 | MPa | ASTM D638, ISO 527-2 |
| -- | 10.0 | MPa | ASTM D638 |
| 4.00 mm | 10.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 10 | % | ASTM D638, ISO 527-2 |
| Fracture | 31 | % | ASTM D638 |
| Fracture, 4.00mm | 31 | % | ISO 527-2 |
| Flexural Modulus (4.00 mm) | 1100 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C, 4.00 mm | 18.9 | kJ/m² | ASTM D256 |
| 23°C, 4.00 mm | 46.2 | kJ/m² | ASTM D256 |
| Notched Izod Impact 1 | ISO 180 | ||
| -20°C | 18 | kJ/m² | ISO 180 |
| 23°C | 46 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | ASTM D256 | ||
| -20°C, 4.00 mm | No Break | ASTM D256 | |
| 23°C, 4.00 mm | No Break | ASTM D256 | |
| Unnotched Izod Impact Strength 2 | ISO 180 | ||
| -20°C | No Break | ISO 180 | |
| 23°C | No Break | ISO 180 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+6 | ohms | ESD STM11.11, IEC 61340-2-3 |
| Volume Resistivity | < 1.0E+4 | ohms·cm | Internal method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 - 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Cylinder Zone 1 Temp. | 200 | °C | |
| Cylinder Zone 2 Temp. | 210 | °C | |
| Cylinder Zone 3 Temp. | 220 | °C | |
| Cylinder Zone 4 Temp. | 220 | °C | |
| Cylinder Zone 5 Temp. | 230 | °C |
| Extrusion instructions |
|---|
| Cylinder Zone 6: 230°C |
| Note Message | |
|---|---|
| 1 . | 4 mm thickness |
| 2 . | 4 mm thickness |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8690-85 Clear Blue 841 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ENVIROPLAS® ENV11-NC720 | ENVIROPLAS®, Inc. | PC | ENVIROPLAS® |
| Osterlene® PPH-3.5-LWC | Osterman & Company | PP Homopolymer | Osterlene® |
| Hifax TYC 852P E C12716 | LyondellBasell Industries | PP Copolymer | Hifax |
| SABIC® BR 4010 | Saudi Basic Industries Corporation (SABIC) | PBR, High Cis | SABIC® BR |