ELITE™ AT 6101
| Category: | EPE , Enhanced Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ELITE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nWSart_ELITE-AT-6101.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ELITE™ AT 6101 Enhanced Polyethylene Resin is a copolymer produced via INSITE™ technology from Dow. It is designed for stretch hooder application and offers a unique combination of holding force, elastic recovery, optics and toughness. Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Puncture Energy | 5.65 | J | Internal method |
| Film Puncture Force | 57.8 | N | Internal method |
| Film Puncture Resistance | 29.0 | J/cm³ | Internal method |
| Film strength | ASTM D882 | ||
| MD | 66.2 | J/cm³ | ASTM D882 |
| TD | 70.3 | J/cm³ | ASTM D882 |
| secant modulus | ASTM D882 | ||
| 1% secant, MD | 88.3 | MPa | ASTM D882 |
| 2% secant, MD | 82.7 | MPa | ASTM D882 |
| 1% secant, TD | 89.6 | MPa | ASTM D882 |
| 2% secant, TD | 82.7 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 5.86 | MPa | ASTM D882 |
| TD : Yield | 5.52 | MPa | ASTM D882 |
| MD : Fracture | 44.8 | MPa | ASTM D882 |
| TD : Fracture | 37.9 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 390 | % | ASTM D882 |
| TD : Fracture | 500 | % | ASTM D882 |
| Dart Drop Impact | 800 | g | ASTM D1709B |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD | 200 | g | ASTM D1922 |
| TD | 360 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 95.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 101 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 75 | ASTM D2457 | |
| Haze | 4.0 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件 螺杆尺寸：3.5英寸 螺杆类型：DSBII 模具间隙：70密耳 熔化温度：421华氏度 产量：12磅/小时/英寸（模具周长） 模具直径：8英寸 模膜直径比：2.5:1 螺杆转速：38 rpm 霜白线高度：58 英寸 |
| Note Message | |
|---|---|
| 1 . | Method B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AKROMID® A3 GF 20 black (2426) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| APEX® 79-B427D-21H | Teknor Apex Company | PVC, Flexible | APEX® |
| COTENE™ M1108 DIP | ICO Polymers EMEA, A Division of A. Schulman | Polyolefin, Unspecified | COTENE™ |
| DURAFIDE® 1140A6 | Polyplastics Co., Ltd. | PPS | DURAFIDE® |
| Interpol 47-5118/47-5205 | Cook Composites and Polymers | PUR-Ester | Interpol |