CYCOLAC™ MGABS02 resin
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nVB2Qi_CYCOLAC-MGABS02-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| General purpose ABS. Excellent flow/impact. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 5.6 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 18.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.80 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2140 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 40.7 | MPa | |
| Break | 31.7 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 2.0 | % | |
| Break | 20 | % | |
| Flexural Modulus 4(50.0 mm Span) | 2210 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 68.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 290 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C, Total Energy) | 30.3 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 96.7 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 82.2 | °C | |
| Vicat Softening Temperature | 98.9 | °C | ASTM D1525 6 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 8.8E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 8.8E-5 | cm/cm/°C | |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI Str | 60.0 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Arc Resistance 7 | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 3 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.52 mm) | HB | UL 94 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (240°C, 1000 sec^-1) | 225 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 to 93.3 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Suggested Shot Size | 50 to 70 | % | |
| Rear Temperature | 188 to 210 | °C | |
| Middle Temperature | 204 to 227 | °C | |
| Front Temperature | 216 to 238 | °C | |
| Nozzle Temperature | 218 to 260 | °C | |
| Processing (Melt) Temp | 218 to 260 | °C | |
| Mold Temperature | 48.9 to 71.1 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm | |
| Vent Depth | 0.038 to 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | Rate B (120°C/h), Loading 2 (50 N) |
| 7 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| XANTAR® SF 22 (Foamed) | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| Ecollent™ PC | Lucent Polymers, Inc. | PC | Ecollent™ |
| Geon™ Vinyl Rigid Extrusion 87736 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| G-Lene PB48A004 | Gas Authority of India Limited | HDPE | G-Lene |
| Moplen HP500N | LyondellBasell Industries | PP Homopolymer | Moplen |