| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | Borealis AG |
| Trademark: | Bormed™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nUgCIN_Bormed-RD804CF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Bormed RD804CF is a random copolymer with low ethylene content. This grade is suitable for the manufacturing of non-oriented cast films on chill roll process, blown films on tubular water quenching process as well as injection moulding and ISBM (2-stage process) for ampoules and bottles. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Molecular Weight Distribution | Narrow | ISO 11357-3 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus (Injection Molded) | 1000 | MPa | ISO 178 |
| Coefficient of Friction | > 0.70 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| MD : 50 µm | 600 | MPa | |
| TD : 50 µm | 600 | MPa | |
| Tensile Strength | ISO 527-3 | ||
| MD : 50 µm | 40.0 | MPa | |
| TD : 50 µm | 30.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break | 550 | % | |
| TD : Break | 600 | % | |
| Instrumented Dart Impact (50 µm, Total Energy) | 17.0 | J | ISO 7765-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 150 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°, 50.0 µm) | > 130 | ASTM D2457 | |
| Haze (50.0 µm) | 1.5 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RONFALIN® ASA35UEF | A. Schulman Europe | ASA | RONFALIN® |
| Miraprene® QS1624D | Mitsubishi Chemical Corporation | TPO (POE) | Miraprene® |
| Shuman PS 811 | Shuman Plastics, Inc. | PS (MIPS) | Shuman PS |
| Nycal™ 1850 | Technical Polymers, LLC | Nylon 6 | Nycal™ |
| Lumid® GP2301BF | LG Chem Ltd. | Nylon 66 | Lumid® |