AXELERON™ GP D-0588 BK CPD Datasheet,LDPE,The Dow Chemical Company-SHANGHAI SUSHENG

Message
AXELERON™ GP D-0588 BK CPD, with a density of 0.93, and a melt index of 0.2, is a prime quality telephone telecom cable black jacketing compound ("CPD"). It offers excellent environmental stress cracking resistance, outdoor weatherability, toughness, low temperature performance, and extrudability. AXELERON™ GP D-0588 BK CPD can be used by wire and cable manufacturers for the entire range of telephone telecom cable sizes and configurations. It is suitable for both aircore and jelly-filled construction, and in both aerial and buried applications. Specifications AXELERON™ GP D-0588 BK CPD meets the following raw material specifications: ASTM D 1248 IC-5 Grades, E5, J1 J3 ISO 1872-1-PE, KCHL, 23-D003 Federal LP-390 C, III-L, Grades 2,3, and 4, Category 5 REA PE-22, 38, 39, 86, 89, 90 Cable jacketed with AXELERON™ GP D-0588 BK CPD using sound commercial extrusion practices, should meet the following specifications: ICEA: S-61-402; NEMA WC 5 ANSI: C8. 35 ASTM: D 2308 British Telecommunications plc M132 Telcordia GR 421 Core ANSI/ICEA S-84-608-1988 EN 50290-2-24, grade LD IEC 60708 BS 6234: Type 03C, TS1

General Information
Uses	Telephone lead wire sheath material Cable sheath Wire and cable applications Wire sheath Coaxial cable sheath material
Agency Ratings	ANSI C 8.35 ASTM D 1248, I, Class C, Cat. 5, Grade E5 ASTM D 1248, I, Class C, Cat. 5, Grade J3 BS 6234 Type 03C, TS1 EN 50290-2-24 FED L-P-390C, Type III, Class L, Category 5, Grade 4 ICEA S-61-402 ICEA S-84-608 IEC 60708 ISO 1872 PE KCHL 23D003 REA PE-22 REA PE-38 REA PE-39 REA PE-89
Forms	Particle

Physical	Nominal Value	Unit	Test Method
Density	0.931	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	0.21	g/10 min	ASTM D1238
Environmental Stress-Cracking Resistance
10% Igepal, F0 ¹	> 2000	hr	IEC 60811-4-1/B
100% Igepal, F20	> 500	hr	ASTM D1693
Carbon Black Content	2.6	%	ASTM D1603
Absorption Coefficient - (kAB/m)	> 400		ASTM D3349

Thermal	Nominal Value	Unit	Test Method
Oxidation Induction Time			ISO 11357-6
200°C	74	min	ISO 11357-6
210°C	30	min	ISO 11357-6

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D, 15 sec)	50		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ²			ASTM D638
Yield	9.31	MPa	ASTM D638
--	17.6	MPa	ASTM D638
Tensile Elongation ³(Break)	800	%	ASTM D638

Thermal	Nominal Value	Unit	Test Method
Brittleness Temperature	< -90.0	°C	ASTM D746

Electrical	Nominal Value		Test Method
Dielectric Constant (1 Hz)	2.48		ASTM D1531
Dissipation Factor (1 MHz)	3.0E-4		ASTM D1531

Extrusion	Nominal Value	Unit
Melt Temperature	204 - 227	°C

Extrusion instructions
AXELERON™ GP D-0588 BK CPD provides excellent surface finish and outstanding output rates over a broad range of conditions. For optimum results, use melt extrusion temperatures in the suggested range of 400°F-440°F (200°C-235°C). However, specific recommendations for processing conditions can be determined only when the application and type of processing equipment are known.This product contains a low moisture absorption carbon black and does not normally need drying. Under extremely high moisture conditions, there is some tendency for the carbon black to absorb moisture. If needed, hopper drying at 150°F-160°F (67°C-71°C) is recommended.

Extrusion instructions

AXELERON™ GP D-0588 BK CPD provides excellent surface finish and outstanding output rates over a broad range of conditions. For optimum results, use melt extrusion temperatures in the suggested range of 400°F-440°F (200°C-235°C). However, specific recommendations for processing conditions can be determined only when the application and type of processing equipment are known.This product contains a low moisture absorption carbon black and does not normally need drying. Under extremely high moisture conditions, there is some tendency for the carbon black to absorb moisture. If needed, hopper drying at 150°F-160°F (67°C-71°C) is recommended.

Note Message
1 .	Without oven conditioning.
2 .	Type 4, 51mm/min
3 .	Type 4, 51mm/min

Category:	LDPE , Black Low Density Polyethylene Compound for Cable Jacketing
Manufacturer:	The Dow Chemical Company
Trademark:	AXELERON™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	nU7wiK_AXELERON-GP-D-0588-BK-CPD.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Miflon® 3231	Jiangsu Meilan Chemical Co., Ltd.	PTFE	Miflon®
Telcar® TL-2585A	Teknor Apex Company	TPE	Telcar®
Staramide BT6	Eurostar Engineering Plastics	Nylon 6	Staramide
Chemlon® 60CF6	Teknor Apex Company (Chem Polymer)	Nylon 6	Chemlon®
Karina BLACK PVC COMPOUND 701D48/ 1-A-IS	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina