Polytron® P40N011
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | Polytron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nS9wb2_Polytron-P40N011.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A CHEMICALLY COUPLED 40% LONG GLASS FIBER REINFORCED NATURAL POLYPROPYLENE HEAT STABILIZED FOR INJECTION MOULDING APPLICATION. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 0.25 to 0.40 | % | |
| -- | 0.25 to 0.40 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9000 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 130 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 2.2 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 9500 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 200 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 20 | kJ/m² | |
| 23°C | 22 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 55 | kJ/m² | |
| 23°C | 80 | kJ/m² | |
| Notched Izod Impact | |||
| 23°C | 200 | J/m | ASTM D256 |
| 23°C | 20 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 152 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 168 | °C | ISO 11357-3, ASTM D3418 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 | |
| Flammability | 22 | mm/min | FMVSS 302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAXAMID™ 136F6Q32 | SAX Polymers | Nylon 6 | SAXAMID™ |
| Chansieh Phenolic J-160R | Chansieh Enterprises Co., LTD. | Phenolic | Chansieh Phenolic |
| KYDEX® T MB | SEKISUI Polymer Innovations, LLC | PMMA+PVC | KYDEX® |
| Durethan® DP 2801 000000 | LANXESS Corporation | Nylon 66 | Durethan® |
| VALOX™ VIC4311 resin | SABIC Innovative Plastics | PBT | VALOX™ |