Niretan B F30
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Soredi S.p.a. |
| Trademark: | Niretan B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nRvyrW_Niretan-B-F30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6 reinforced with 30% glass fibre, for injection moulding |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.34 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 to 0.70 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 7.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.5 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | 100 | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength 1(Break) | 170 | 100 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 3.0 | 5.0 | % | ASTM D638 |
| Flexural Modulus 3 | 8000 | 5000 | MPa | ASTM D790 |
| Flexural Strength 4(Break) | 260 | 160 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| -20°C, 3.20 mm | 100 | 160 | J/m | |
| 23°C, 3.20 mm | 140 | 200 | J/m |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 202 | -- | °C | ASTM D648 |
| Peak Crystallization Temperature (DSC) | 220 | -- | °C | ASTM D3418 |
| CLTE - Flow (23 to 55°C) | 4.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength (1.00 mm) | 34 | 24 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.80 | 4.20 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.020 | 0.12 | IEC 60250 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | ||
| 3.20 mm | HB | -- | ||
| Glow Wire Ignition Temperature (2.00 mm) | 650 | -- | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SynPlast™ 810TM-E | PolyOne Corporation | Tri (n-octyl, n-decyl) Trimellitate | SynPlast™ |
| Armlen® PP IC 50-1 | Poly Plastic | PP, Unspecified | Armlen® |
| Celstran® PBT-GF30-08 | Celanese Corporation | PBT | Celstran® |
| Evoprene™ LF 6151 | AlphaGary | SBC | Evoprene™ LF |
| Fainplast PVC KL 52/V | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |