LNP™ STAT-KON™ DD0009 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nRqkCD_LNP-STAT-KON-DD0009-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON DD0009 is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material include: Electrically Conductive, Flame Retardant. Also known as: LNP* STAT-KON* Compound D-FR Product reorder name: DD0009 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 | g/cm³ | ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.80 | % | ASTM D955 |
| Across Flow : 24 hr | 0.70 | % | ASTM D955 |
| Across Flow : 24 hr | 0.72 | % | ISO 294-4 |
| Flow : 24 hr | 0.75 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.18 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.27 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2830 | MPa | ASTM D638 |
| -- | 2810 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 61.9 | MPa | ASTM D638 |
| Yield | 62.8 | MPa | ISO 527-2 |
| Break | 53.9 | MPa | ASTM D638 |
| Break | 57.1 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 1.2 | % | ASTM D638 |
| Yield | 4.2 | % | ISO 527-2 |
| Break | 5.6 | % | ASTM D638 |
| Break | 7.5 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2830 | MPa | ASTM D790 |
| -- | 2880 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 108 | MPa | ASTM D790 |
| -- | 102 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 68 | J/m | ASTM D256 |
| 23°C 2 | 6.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1600 | J/m | ASTM D4812 |
| 23°C 3 | 71 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 10.9 | J | ASTM D3763 |
| -- | 5.70 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 141 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 139 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 133 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 131 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 5.4E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 5.7E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+4 to 1.0E+6 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.70 mm, Testing by SABIC) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1405 TFE 15 | RTP Company | PESU | RTP |
| RTP ESD A 204 H | RTP Company | Nylon 66 | RTP |
| Santoprene™ 101-73 | ExxonMobil Chemical | TPV | Santoprene™ |
| ALAMID® 6.6 S NATUR-9142 | LEIS Polytechnik - polymere Werkstoffe GmbH | Nylon 66 | ALAMID® |
| KPOL-PP K-PPH 5.0 | KPOL Chem Co. | PP Homopolymer | KPOL-PP |