LNP™ LUBRICOMP™ QAP22S compound
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nRiDvC_LNP-LUBRICOMP-QAP22S-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP QAP22S is a compound based on Nylon 6/10 resin containing 10% PTFE/Silicone, 10% Aramid Fiber. Added features of this material include: Wear Resistant, Heat Stabilized. Also known as: LNP* LUBRICOMP* Compound QAL-4522 HS Product reorder name: QAP22S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 1.0 | % | |
| Across Flow : 24 hr | 1.8 | % | |
| Water Absorption (24 hr, 50% RH) | 0.30 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3450 | MPa | ASTM D638 |
| -- | 3310 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 45.5 | MPa | ASTM D638 |
| Yield | 50.0 | MPa | ISO 527-2 |
| Break | 45.5 | MPa | ASTM D638 |
| Break | 50.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 1.8 | % | ASTM D638 |
| Yield | 2.3 | % | ISO 527-2 |
| Break | 1.8 | % | ASTM D638 |
| Break | 2.3 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2760 | MPa | ASTM D790 |
| -- | 3000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 103 | MPa | ASTM D790 |
| -- | 76.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.41 | ||
| vs. Itself - Static | 0.26 | ||
| Wear Factor - Washer | 11.5 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 37 | J/m | ASTM D256 |
| 23°C 2 | 4.4 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 350 | J/m | ASTM D4812 |
| 23°C 3 | 33 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 1.10 | J | ASTM D3763 |
| -- | 1.40 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 204 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 193 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 119 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 94.0 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 8.5E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 8.4E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 6.3E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 to 0.20 | % | |
| Rear Temperature | 249 to 260 | °C | |
| Middle Temperature | 260 to 271 | °C | |
| Front Temperature | 271 to 282 | °C | |
| Processing (Melt) Temp | 271 to 277 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ F5134T4-1 | PolyOne Corporation | PP Homopolymer | Maxxam™ |
| Tectron H2408 | TECTRON Systems Pte Ltd | TPV | Tectron |
| Clariant ABS ABS3470 | Clariant Corporation | ABS | Clariant ABS |
| POCAN® KL 1-7033 000000 | LANXESS GmbH | PBT | POCAN® |
| LNP™ LUBRICOMP™ RCL36 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |