NILAMID® A3 H GCF3010
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Nilit Plastics |
| Trademark: | NILAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nRgSoz_NILAMID-A3-H-GCF3010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NILAMID® A3 H GCF3010 is a Polyamide 66 (Nylon 66) compound, 30% glass fiber and 10% carbon fiber reinforced, heat stabilized. This compound is intended for injection molding. NILAMID® A3 H GCF3010 is primarily designed for the Automotive industry. It is also suitable for Industrial & Consumer applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.28 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 23°C | 1.2 | % | |
| Flow : 23°C | 1.0 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 1.9 | % | |
| Saturation, 23°C | 6.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 11500 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 155 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.5 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 6.0 | kJ/m² | |
| 23°C | 8.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| 23°C | No Break | ||
| 30°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 250 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | °C | ISO 75-2/A |
| Continuous Use Temperature 1 | 130 | °C | IEC 60216 |
| Ball Pressure Test | IEC 60695-10-2 | ||
| 125°C | Pass | ||
| 165°C | Pass |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 2 | 1.0E+7 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+8 | ohms·cm | IEC 60093 |
| Comparative Tracking Index (3.20 mm, Solution A) | 200 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB | ||
| Oxygen Index | 28 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | 20000 hr |
| 2 . | 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAFORM® 9 A GF 20 | A. Schulman Europe | Acetal (POM) Copolymer | SCHULAFORM® |
| Tenite™ Acetate 105E2R30025 Natural, Trsp | Eastman Chemical Company | CA | Tenite™ Acetate |
| Alpha PVC GW 2409-VW1 NAT 50 LCF | AlphaGary | PVC, Semi-Rigid | Alpha PVC |
| Staramide RF006S | Eurostar Engineering Plastics | Nylon 66 | Staramide |
| SQUARE® LSR8602-50A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |