Kelon® A FR H2 CET/35-V2
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Kelon® A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nReZon_Kelon-A-FR-H2-CET-35-V2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyamide 66 (PA66) based compound. Heat stabilised. Mineral filler. UL94 V-2 classified, with brominated flame retardants, PBB/PBDE free. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.57 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.60 to 0.75 | % | |
| Flow : 2.00 mm | 0.50 to 0.70 | % | |
| Water Absorption (23°C, 24 hr) | 0.27 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 9500 | MPa | |
| 60°C | 7300 | MPa | |
| 90°C | 3800 | MPa | |
| 120°C | 2100 | MPa | |
| 150°C | 1600 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 90°C | 35.0 | MPa | |
| Yield, 120°C | 25.0 | MPa | |
| Yield, 150°C | 20.0 | MPa | |
| Break, 23°C | 70.0 | MPa | |
| Break, 60°C | 55.0 | MPa | |
| Break, 90°C | 35.0 | MPa | |
| Break, 120°C | 25.0 | MPa | |
| Break, 150°C | 20.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 90°C | 6.0 | % | |
| Yield, 120°C | 10 | % | |
| Yield, 150°C | > 10 | % | |
| Break, 23°C | 1.5 | % | |
| Break, 60°C | 2.5 | % | |
| Break, 90°C | 7.0 | % | |
| Break, 120°C | 15 | % | |
| Break, 150°C | 25 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 2.0 | kJ/m² | |
| 23°C | 3.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 25 | kJ/m² | |
| 23°C | 25 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 210 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 165 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 125 | °C | |
| Vicat Softening Temperature | 200 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-2 | ||
| 1.50 mm | V-2 | ||
| 3.00 mm | V-2 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | |
| 2.00 mm | 960 | °C | |
| Oxygen Index | 28 | % | ASTM D2863 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Dimensional Stability | 79.0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Regrind | 15 | % | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 70.0 to 100 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 60 MPa |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMATOP PP CO 005NB | Amco Polymers | PP Copolymer | PRIMATOP |
| Microthene® MP635662 | LyondellBasell Industries | LLDPE | Microthene® |
| Deco-Coat™ DC-2501R | Epoxies, Etc. | Epoxy | Deco-Coat™ |
| Karina BLACK PVC COMPOUND -E 700D48/ 1-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Bergadur™ PB40 G30 | PolyOne Corporation | PBT | Bergadur™ |