Starflam RF0055E
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Starflam |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nRWXSp_Starflam-RF0055E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starflam RF0055E is a Halogen Free and Red Phosphorous Free Flame Retardant, Glass Fiber Reinforced, PA66 / PA6 Injection Molding (also known as RF1005Z250EM) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.47 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (24 hr) | 0.10 to 0.30 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9800 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 140 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2 |
| Flexural Modulus | 8400 | MPa | ISO 178 |
| Flexural Stress | 190 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 1(23°C) | 8.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 2(23°C) | 40 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed, 64.0 mm Span) | 210 | °C | ISO 75-2/Af |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.00 mm | V-1 | ||
| 1.20 mm | V-0 | ||
| 1.60 mm, Tested by E2P | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 265 to 275 | °C | |
| Middle Temperature | 265 to 275 | °C | |
| Front Temperature | 270 to 280 | °C | |
| Processing (Melt) Temp | 270 to 280 | °C | |
| Mold Temperature | 60.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 80*10*4 |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Soarnol® DC3212B | Soarus L.L.C. | EVOH | Soarnol® |
| UBE Nylon 5034 TX18 | UBE Engineering Plastics, S.A. | Nylon 66/6 | UBE Nylon |
| DJSilicone NE-- T-1/NE-T-1U | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Karina BLACK PVC COMPOUND 804-48/ 1-CRM | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Mafill® CG 4210 | Ravago Group | PP Copolymer | Mafill® |