MAJORIS AT360
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nQQgWX_MAJORIS-AT360.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AT360 is a filled talc reinforced, high molecular weight, low melt index flow rate polypropylene block copolymer with a very high stiffness at a good level of impact strength. APPLICATIONS AT360 is recommended for the extrusion of profiles (building, electrical, furniture and construction profiles or pipes). Products made from this material show a high dimensional stability and low process shrinkage. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.60 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3090 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 28.2 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 4.4 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 2.7 | kJ/m² | |
| 23°C | 11 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 75.0 | °C | ISO 306/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Cylinder Zone 1 Temp. | 190 to 230 | °C | |
| Cylinder Zone 3 Temp. | 190 to 230 | °C | |
| Cylinder Zone 5 Temp. | 190 to 230 | °C | |
| Melt Temperature | 200 to 230 | °C | |
| Head Temperature | 200 to 230 | °C | |
| Die Temperature | 200 to 230 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® 9398 | Chevron Phillips Chemical Company LLC | HDPE | Marlex® |
| SEETEC EVA VA600 | Lotte Chemical Corporation | EVA | SEETEC EVA |
| SLOVAMID® 66 GF 30 | Plastcom | Nylon 66 | SLOVAMID® 66 |
| ALTECH® PA6 A 2010/100 GF10 | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| ESTACARB 1560 V0 | Cossa Polimeri S.r.l. | PC | ESTACARB |