TECOLITE KM-1000
| Category: | Phenolic , Phenolic |
| Manufacturer: | KYOCERA Chemical Corporation |
| Trademark: | TECOLITE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nQ33rF_TECOLITE-KM-1000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Environmentally friendly and possible to substitution of metal parts. And High cost performance. Kyocera Chemical's Phenolic molding compounds "TECOLITE" are environmentally friendly molding compounds. These acquired recognize UL94V-0 without any halogenated flame retardant. These compounds have excellent properties in high temperature. Therefore, it is possible to use in high temperature environment for substitution metal parts and various electrical parts. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | 1.80 | g/cm³ | |
| Molding Shrinkage - Flow 1 | 0.60 | % |
| Mechanical | Nominal Value | Unit | |
|---|---|---|---|
| Flexural Modulus | |||
| 23°C | 15500 | MPa | |
| 200°C | 12500 | MPa | |
| Flexural Strength | |||
| 23°C | 195 | MPa | |
| 200°C | 100 | MPa | |
| Compressive Strength | 245 | MPa |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Heat Deflection Temperature | > 250 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Insulation Resistance | |||
| After Boiling | 1.0E+10 | ohms | |
| As Molded | 1.0E+11 | ohms | |
| Dielectric Strength | > 10 | kV/mm | |
| Arc Resistance | 180 | sec |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.810 mm) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | Compression Molding |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-MFC-G30 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| Tenite™ Propionate 380A2R30015 Natural, Trsp | Eastman Chemical Company | CAP | Tenite™ Propionate |
| Wanthane® WHT-1495EC | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | Wanthane® |
| 3M™ Dyneon™ PTFE TF 2029Z | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE |
| ESPOLEX 487X | Sumitomo Chemical America, Inc. | TPO (POE) | ESPOLEX |