KumhoSunny PC/ABS HAC8265P
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | KumhoSunny PC/ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nPKtC8_KumhoSunny-PC-ABS-HAC8265P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC/ABSHAC8265P is a high chemical resistance and super high heat resistance PC/ABS resin.PC/ABSHAC8265P has been widely used in Auto exterior parts, such as handle , hubcap and so on. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.14 | g/cm³ | ISO 1183 |
| Molding Shrinkage (23°C) | 0.50 to 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 58.0 | MPa | ISO 527-2/50 |
| Flexural Modulus 1 | 2300 | MPa | ISO 178 |
| Flexural Stress 2 | 76.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3 | ISO 179 | ||
| -30°C | 35 | kJ/m² | |
| 23°C | 55 | kJ/m² | |
| Charpy Unnotched Impact Strength 4(23°C) | No Break | ISO 179 | |
| Notched Izod Impact Strength 5(23°C) | 52 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 6(1.8 MPa, Unannealed) | 110 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 125 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 220 to 230 | °C | |
| Middle Temperature | 240 to 250 | °C | |
| Front Temperature | 260 to 270 | °C | |
| Nozzle Temperature | 250 to 260 | °C | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Back Pressure | 0.300 to 1.00 | MPa | |
| Screw Speed | 30 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Condition: 4 J |
| 4 . | Condition: 4 J |
| 5 . | Condition: 5.5 J |
| 6 . | 120°C/h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205.3 HS | RTP Company | Nylon 66 | RTP |
| PRL AC-GP3 | Polymer Resources Ltd. | Acetal (POM) Copolymer | PRL |
| Network Polymers SBS 1000 | Network Polymers, Inc. | SBS | Network Polymers SBS |
| ELASTOSIL® LR 3842/50 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| NOVAPOL® HB-W646-UH | NOVA Chemicals | HDPE | NOVAPOL® |