Desmopan® DP 9665DU
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Desmopan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nOKvVL_Desmopan-DP-9665DU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Extrusion- and injection molding grade; with special UV stabilizers; transparent up to 6 mm wall thickness; very good hydrolysis and microbial resistance; Application; Ski boot shells; Hoses, non-reinforced; Pneumatic hoses |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.18 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore A, 23°C | 98 | ||
| Shore D, 23°C | 65 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | DIN 53504 | ||
| Break, 23°C | 53.4 | MPa | |
| 10% Strain, 23°C | 15.8 | MPa | |
| 50% Strain, 23°C | 23.6 | MPa | |
| 100% Strain, 23°C | 28.4 | MPa | |
| 300% Strain, 23°C | 37.8 | MPa | |
| Tensile Strain 2(Break, 23°C) | 350 | % | DIN 53504 |
| Flexural Modulus 3(23°C) | 270 | MPa | ISO 178 |
| Abrasion Resistance (23°C) | 19.0 | mm³ | ISO 4649-A |
| Tensile Storage Modulus | ISO 6721-1,-4 | ||
| -20°C | 2.25 | GPa | |
| 20°C | 0.816 | GPa | |
| 60°C | 0.215 | GPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Resilience (23°C) | 40 | % | ISO 4662 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 4(23°C) | 210 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 72 hr | 39 | % | |
| 70°C, 24 hr | 53 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 110 | °C | |
| Processing (Melt) Temp | 220 to 235 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 110 | °C | |
| Melt Temperature | 205 to 235 | °C |
| Note Message | |
|---|---|
| 1 . | 200 mm/min |
| 2 . | 200 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom PP6225 E49 | Spartech Polycom | PP, Unspecified | Spartech |
| Vibrathane® B629 | Chemtura | PUR-Ether/TDI | Vibrathane® |
| Vydyne® ECO315 BK06 | Ascend Performance Materials Operations LLC | Nylon 66/6 | Vydyne® |
| Cheng Yu FRCV150 | Cheng Yu Plastic Company Limited | Nylon 66 | Cheng Yu |
| INDURE™ X210A | LyondellBasell Industries | TPO (POE) | INDURE™ |