ALCUDIA® EVA PA-539
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | REPSOL |
| Trademark: | ALCUDIA® EVA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nO5G83_ALCUDIA-EVA-PA-539.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EVA copolymer ALCUDIA® PA-539 is suitable for film extrusion and extrusion coating. This material combines easy processability with excellent mechanical and optical properties. It contains antioxidant additives. TYPICAL APPLICATIONS
Recommended melt temperature below 200°C to avoid the decomposition of the polymer. Processing conditions should be optimised for each production line. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.937 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance (F50) | > 300 | hr | ASTM D1693 |
| Vinyl Acetate Content | 18.0 | wt% |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | 26.0 | MPa | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 22.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | 320 | % | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 640 | % | ISO 527-3 |
| Dart Drop Impact (50 µm, Blown Film) | 600 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 50 µm, blown film | 2.0 | N | ISO 6383-2 |
| TD : 50 µm, blown film | 2.8 | N | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 64.0 | °C | ISO 306/A |
| Melting Temperature | 87.0 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (50.0 µm, Blown Film) | 4.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Data taken from 50 µm thickness film, blow up ratio 2.25:1, frost line height 40 cm. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVAMID® 66 GF 30 HTS | Plastcom | Nylon 66 | SLOVAMID® 66 |
| FARALLOY® PE-401 | O'Neil Color and Compounding | LLDPE | FARALLOY® |
| Flexathene® TP4311HC | LyondellBasell Industries | Polyolefin, Unspecified | Flexathene® |
| EMPOL® BV 107 FR V0 | EMAS Plastik San.Tic.AS. | PS (GPPS) | EMPOL® |
| SABIC® PPcompound 15T1020 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |