Texin® 1210
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Texin® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nO4rCS_Texin-1210.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Texin 1210 resin is an aromatic polyester-based thermoplastic polyurethane with a Shore hardness of approximately 92A. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792, ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 92 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | ASTM D790, ISO 178 | ||
| 23°C | 73.1 | MPa | ASTM D790, ISO 178 |
| 70°C | 31.7 | MPa | ASTM D790, ISO 178 |
| Taber Abrasion Resistance | |||
| 1000 Cycles, 1000g, H-18 wheel | 27.0 | mg | ISO 4649 |
| 1000 Cycles, 1000g, H-18 wheel | 27.0 | mg | ASTM D1044 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412, ISO 37 | ||
| 100% strain | 9.70 | MPa | ASTM D412, ISO 37 |
| 300% strain | 20.0 | MPa | ASTM D412, ISO 37 |
| Tensile Strength (Yield) | 40.0 | MPa | ASTM D412, ISO 37 |
| Tensile Elongation (Break) | 510 | % | ASTM D412, ISO 37 |
| Tear Strength | |||
| -- 1 | 129 | kN/m | ASTM D624 |
| -- | 130 | kN/m | ISO 34-1 |
| Compression Set 2 | ASTM D395B, ISO 815 | ||
| 23°C, 22 hr | 16 | % | ASTM D395B, ISO 815 |
| 70°C, 22 hr | 43 | % | ASTM D395B, ISO 815 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -14.0 | °C | DMA |
| Vicat Softening Temperature | 88.0 | °C | ISO 306/50, ASTM D1525 3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 81.0 - 104 | °C | |
| Drying Time - Desiccant Dryer | 2.0 | hr | |
| Suggested Max Moisture | < 0.030 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 182 - 196 | °C | |
| Middle Temperature | 188 - 204 | °C | |
| Front Temperature | 193 - 207 | °C | |
| Nozzle Temperature | 196 - 210 | °C | |
| Processing (Melt) Temp | 191 - 204 | °C | |
| Mold Temperature | 16.0 - 38.0 | °C | |
| Injection Pressure | 41.4 - 103 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | < 5.52 | MPa | |
| Screw Speed | 40 - 80 | rpm | |
| Cushion | < 3.18 | mm |
| Injection instructions |
|---|
| Hold Pressure: 60 to 80% of Injection Pressure |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 81.0 - 104 | °C | |
| Drying Time | 2.0 | hr | |
| Cylinder Zone 1 Temp. | 182 - 199 | °C | |
| Cylinder Zone 2 Temp. | 182 - 204 | °C | |
| Cylinder Zone 3 Temp. | 182 - 204 | °C | |
| Melt Temperature | 191 - 204 | °C | |
| Die Temperature | 188 - 204 | °C |
| Note Message | |
|---|---|
| 1 . | C mould |
| 2 . | Post-cured 16 hr at 230°F |
| 3 . | 速率 A (50°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Clear Cote™ TECHNO-COTE™ | Club Kit, Inc. | Epoxy | Clear Cote™ |
| Flontech® FT-EK10-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| ESENTTIA 40H92 | Polipropileno del Caribe S.A. | PP Homopolymer | ESENTTIA |
| Panlite® ML-6500ZAL | TEIJIN LIMITED | PC | Panlite® |
| Polifil® Nylon 628L-13GF | The Plastics Group | Nylon 66 | Polifil® Nylon |