Lumid® EG2309B(W)
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lumid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nNbUGL_Lumid-EG2309B-W-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description Chemical Resistance(CaCl2, Ethylene Glycol) Application Radiator Tank, Intercooler Tank |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.90 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.70 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break, 6.40 mm) | 177 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 6.40 mm) | 4.0 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 8140 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 6.40 mm) | 255 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.20 mm | 110 | J/m | |
| 23°C, 6.40 mm | 98 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 260 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 250 | °C | |
| Peak Melting Temperature | 260 | °C | ASTM D3418 |
| CLTE - Flow | 3.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C, 1.00 mm) | 25 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C, 1 MHz) | 4.00 | ASTM D150 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Suggested Max Moisture | < 0.080 | % | |
| Rear Temperature | 260 to 270 | °C | |
| Middle Temperature | 270 to 285 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Nozzle Temperature | 270 to 295 | °C | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Back Pressure 5 | 0.981 to 2.94 | MPa | |
| Screw Speed | 60 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | Hydraulic Type |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIME TPO R110MP | Prime Polymer Co., Ltd. | PP Impact Copolymer | PRIME TPO |
| TOPAS® 6013M-07 | Topas Advanced Polymers, Inc. | COC | TOPAS® |
| Viton® GFLT-200S | DuPont Performance Elastomers | Fluorelastomer | Viton® |
| NEALID XG370 | AD majoris | Nylon+Olefin | NEALID |
| AKROMID® B3 3 S3 10 black 950063 (1809) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |