Terluran® SP-6
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | INEOS Styrolution Group GmbH |
| Trademark: | Terluran® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nNXcXd_Terluran-SP-6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Terluran SP-6 is a high impact extrusion grade. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 5.50 | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 1.0 | % | |
| Equilibrium, 23°C, 50% RH | 0.21 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 74.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1900 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 38.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 2.8 | % | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 9.0 | % | ISO 527-2 |
| Flexural Stress | 56.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 13 | kJ/m² | |
| 23°C | 35 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 140 | kJ/m² | |
| 23°C | No Break | ||
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 14 | kJ/m² | |
| 23°C | 36 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Annealed | 97.0 | °C | ISO 75-2/B |
| 1.8 MPa, Annealed | 93.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 103 | °C | ISO 306/A50 |
| -- | 90.0 | °C | ISO 306/B50 |
| CLTE - Flow | 8.0E-5 to 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.17 | W/m/K | DIN 52612 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 2.90 | ||
| 1 MHz | 2.80 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 5.4E-3 | ||
| 1 MHz | 8.2E-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Yellowness Index | 15 | YI | DIN 6167 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Melt Temperature | 200 to 240 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TechnoDur PBT-PET GF15 black (9971) | TechnoCompound GmbH | PBT+PET | TechnoDur |
| Desmopan® DP 6072A | Covestro - PUR | TPU, Unspecified | Desmopan® |
| ETILINAS HD5740UA | POLYETHYLENE MALAYSIA SDN BHD | HDPE | ETILINAS |
| Hifax CB228 | LyondellBasell Industries | TPO (POE) | Hifax |
| Karina BLACK PVC COMPOUND TR-550D48/ 1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |