Tenac™ GN705
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | Tenac™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nNOF0Y_Tenac-GN705.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Tenac™ GN705 is an Acetal (POM) Homopolymer product filled with glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of Tenac™ GN705 include engineering/industrial parts and housings. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.56 | g/cm³ | ASTM D792 |
| -- | 1.59 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow | 0.40 to 0.60 | % | |
| Across Flow | 1.0 to 1.3 | % | |
| Water Absorption (23°C, 24 hr, 50% RH) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 90 | ||
| R-Scale | 120 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9000 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Break | 110 | MPa | ISO 527-2 |
| -- | 106 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Break | 6.0 | % | ASTM D638 |
| Break | 2.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 8200 | MPa | ASTM D790 |
| -- | 8500 | MPa | ISO 178 |
| Flexural Strength | 173 | MPa | ASTM D790 |
| Taber Abrasion Resistance | 23.0 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 7.0 | kJ/m² | ISO 179 |
| Notched Izod Impact | 66 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 174 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 175 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 170 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 171 | °C | ISO 75-2/A |
| CLTE | |||
| Flow | 4.0E-5 | cm/cm/°C | ASTM D696 |
| Flow | 4.0E-5 to 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.750 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Restramid PA 6 50GF | Polimarky Spolka Jawna | Nylon 6 | Restramid |
| Xuchuan XCD-650 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| NEFTEKHIM PP 8332C (EPD60R) | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| Rotuba CAP CP801 (18% Plasticizer) | Rotuba Extruders, Inc. | CAP | Rotuba CAP |
| Pearlbond™ D1160 | Lubrizol Advanced Materials, Inc. | TPU, Unspecified | Pearlbond™ |