MAJORIS GFR450
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nNEtQa_MAJORIS-GFR450.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAJORIS GFR450 is a special long glass fibre reinforced polypropylene compound halogen free flame retardant UL 94 VO classification, for injection moulding and extrusion. The long glass fibres, chemically coupled to the polypropylene matrix, are providing with outstanding mechanical properties. MAJORIS GFR450 is available both in natural (MAJORIS GFR450) and black (MAJORIS GFR450-8229). Other colours can be provided on request. APPLICATIONS MAJORIS GFR450 is intended for injection moulding of highly demanding technical applications. The excellent properties of MAJORIS GFR450 make it suitable for:
MAJORIS GFR450 can, in many of these applications, substitute other engineering plastics or metal alloys. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction : 2.00mm | 0.74 | % | ISO 294-4 |
| Flow direction : 2.00mm | 0.32 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 80.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 9000 | MPa | ISO 178 |
| Flexural Stress | 130 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 17 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 20 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 162 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 150 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (2.00 mm) | 825 | °C | IEC 60695-2-13 |
| Oxygen Index 2 | 35 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 180 - 220 | °C | |
| Processing (Melt) Temp | 180 - 220 | °C | |
| Mold Temperature | 60.0 - 100 | °C | |
| Injection Pressure | 30.0 - 60.0 | MPa | |
| Injection Rate | Slow | ||
| Screw Speed | 30 - 150 | rpm |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressureBack pressure: as low as possible, 0 to 10%Holding time: as long as practical |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer KE-951U | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| Spartech Polycom SCR7-7006UR | Spartech Polycom | PC | Spartech |
| Staramide BG3H | Eurostar Engineering Plastics | Nylon 6 | Staramide |
| TAIRIREX MP6500 | Formosa Plastics Corporation | PS (MIPS) | TAIRIREX |
| Unichem 6284 | Colorite Polymers | PVC, Unspecified | Unichem |