VESTAMID® HTplus C2505
| Category: | PPA , Polyphthalamide |
| Manufacturer: | Evonik Industries AG |
| Trademark: | VESTAMID® HTplus |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nMtgEL_VESTAMID-HTplus-C2505.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VESTAMID HTplus C2505 is a freeze ground powder based on a PA10T-copolyamide. PA10T is a polycondensation product of 1,10-decamethylene diamine (10) and terephthalic acid (T). As 1,10-decamethylene diamine is derived from castor oil plants, VESTAMID HTplus C2505 is partially natural resourced and thus bio-based. VESTAMID HT plus C2505 exhibits a particle size up to 63 µm. This powder resin is especially suited for manufacturing parts subjected to high temperature. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.11 | g/cm³ | ISO 1183 |
| Particle Size Distribution | |||
| d 10 | 20.0 | µm | |
| d 50 | 50.0 | µm | |
| d 90 | 80.0 | µm |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2100 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 62.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 100 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C, Complete Break | 15 | kJ/m² | |
| 23°C, Complete Break | 18 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -40°C, Complete Break | > 100 | kJ/m² | |
| 23°C, Complete Break | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 130 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 124 | °C | ISO 75-2/A |
| Melting Temperature (DSC) 1 | 265 | °C | ISO 11357 |
| Note Message | |
|---|---|
| 1 . | 2nd heating |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SHIN-A SEB-350 | SHIN-A T&C | Epoxy | SHIN-A |
| ACCUTECH™ HP0339C20L | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Exelene® PP R3505 | Montachem International, Inc. | PP Random Copolymer | Exelene® PP |
| IPC PP 4820C-T | International Polymers Corporation | PP Copolymer | IPC PP |
| 3M™ Dyneon™ Fluoroelastomer FC 2144 | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |