Vydyne® R525J NT0721
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ascend Performance Materials Operations LLC |
| Trademark: | Vydyne® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | nMHBED_VydyneR525JNT0721.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| R525J NT0721 is a natural, 25% glass-filled, high-flow PA66 that is heat-stabilized with an electrically neutral heat stabilizer. It is specially designed for electrical applications requiring high dielectric strength, low conductivity and corrosion resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.32 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Lateral flow : 23°C, 2.00mm | 0.90 | -- | % | ISO 294-4 |
| Traffic : 23°C, 2.00mm | 0.40 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 0.90 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.0 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 8600 | 5500 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 174 | 117 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 3.0 | 7.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 7700 | 5700 | MPa | ISO 178 |
| Flexural Stress (23°C) | 250 | 150 | MPa | ISO 178 |
| Poisson's Ratio | 0.40 | -- | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 10 | 10 | kJ/m² | ISO 179/1eA |
| 23°C | 11 | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 55 | 66 | kJ/m² | ISO 179/1eU |
| 23°C | 65 | 67 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180 | |||
| -30°C | 9.0 | 10 | kJ/m² | ISO 180 |
| 23°C | 10 | 15 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 258 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 245 | -- | °C | ISO 75-2/A |
| Melting Temperature | 260 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C, 2.00mm | 2.5E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C, 2.00mm | 1.1E-4 | -- | cm/cm/°C | ISO 11359-2 |
| RTI Elec | UL 746 | |||
| 0.75 mm | 120 | -- | °C | UL 746 |
| 1.5 mm | 120 | -- | °C | UL 746 |
| 3.0 mm | 120 | -- | °C | UL 746 |
| RTI Imp | UL 746 | |||
| 0.75 mm | 85.0 | -- | °C | UL 746 |
| 1.5 mm | 85.0 | -- | °C | UL 746 |
| 3.0 mm | 105 | -- | °C | UL 746 |
| RTI | UL 746 | |||
| 0.75 mm | 115 | -- | °C | UL 746 |
| 1.5 mm | 120 | -- | °C | UL 746 |
| 3.0 mm | 120 | -- | °C | UL 746 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity (0.750 mm) | 1.0E+13 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength (1.00 mm) | 24 | -- | kV/mm | IEC 60243 |
| Arc Resistance (3.00 mm) | PLC 5 | -- | ASTM D495 | |
| Comparative Tracking Index (3.00 mm) | 600 | -- | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | UL 746 | |||
| 0.75 mm | PLC 0 | -- | UL 746 | |
| 1.5 mm | PLC 0 | -- | UL 746 | |
| 3.0 mm | PLC 0 | -- | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 1 | -- | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | |||
| 0.75 mm | PLC 4 | -- | UL 746 | |
| 1.5 mm | PLC 4 | -- | UL 746 | |
| 3.0 mm | PLC 4 | -- | UL 746 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.75 mm | HB | -- | UL 94 | |
| 1.5 mm | HB | -- | UL 94 | |
| 3.0 mm | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 280 - 310 | °C | |
| Middle Temperature | 280 - 310 | °C | |
| Front Temperature | 280 - 310 | °C | |
| Nozzle Temperature | 280 - 310 | °C | |
| Processing (Melt) Temp | 285 - 305 | °C | |
| Mold Temperature | 65 - 95 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Thermylene® P1-35FM-Y942 | Asahi Kasei Plastics North America Inc. | PP, Unspecified | Thermylene® |
| Visico™ LE0540 | Borealis AG | XLPE | Visico™ |
| Nylfor® 74S5251PO 0001 | SO.F.TER. SPA | Nylon 66 | Nylfor® |
| Hypro® PP- CP 35/1.5C | Entec Polymers | PP Impact Copolymer | Hypro® |
| PENTAMID A GV30 HYD schwarz | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |